Experimental study of thermomechanical behaviour of Gum Metal during cyclic tensile loadings: the quantitative contribution of IRT and DIC

Thermomechanical behaviour of Gum Metal (Ti-23Nb-0.7Ta-2.0Zr-1.2O, at.%) under cyclic tension was experimentally investigated using infrared thermography and digital image correlation. The thermomechanical characteristics of particular stages of the subsequent loading-unloading cycles of Gum Metal were identified, i.e. (I) the linear, elastic loading accompanied by the temperature drop, (II) the nonlinear super-elastic loading related to the temperature growth, (III) the transient stage (at which both the superelastic-like behaviour and the plastic one are present simultaneously) and the temperature starts growing fast, (IV) the plastic deformation with a significant growth of temperature, (V) the superelastic-like unloading accompanied by a fast drop in temperature, (VI) the transient unloading with a slower decrease in temperature and (VII) the elastic unloading, with a slight increase in temperature. Thermoelastic effect in Gum Metal during both loading and unloading was analysed in each tensile cycle. Finally, the evolution of strain and temperature fields just before unloading in each cycle was discussed and a comparison of the fields at selected stages of cycles 12 and 24 was presented. The results of this work enabled us to identify the non-dissipative processes of elastic and superelastic-like deformations as well as the dissipative process of plastic deformation.