Effect of Ni content on the microstructure and properties of WCoB-TiC cermets

被引:1
|
作者
Zhu, Xingyu [1 ]
Pan, Yingjun [1 ]
Zhang, Hao [2 ]
Ke, Deqing [1 ]
机构
[1] Wuhan Univ Sci & Technol, State Key Lab Refractories & Met, Wuhan 430081, Peoples R China
[2] Zhejiang Ind & Trade Vocat Coll, Coll Optoelect Mfg, Wenzhou 325003, Peoples R China
关键词
Vacuum liquid phase sintering; WCoB-TiC cermet; Vickers hardness; Fracture toughness; Tribological properties; FRACTURE-TOUGHNESS; MECHANICAL-PROPERTIES;
D O I
10.1016/j.ijrmhm.2023.106381
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
To expand the applications of WCoB ternary borides in industry, the effect of Ni addition to WCoB-TiC cermets on their microstructures and properties was investigated in this study. Most of the Ni added was in the binder phase, forming a solid solution with Co. Although traces of Ni were dissolved in the hard phase, no new hard phase was generated. The thickness of the elongated hard phase increased with increasing Ni content. The sample with a Ni content of 15 wt% had the maximum Vickers hardness of 2102.5 HV0.5 at a fracture toughness of 9.84 MPa center dot m(1/2). The hardness and fracture toughness of the sample increased by 14.8% and 14.2%, respectively, when compared with the corresponding values of the sample with no added Ni. The fractures in the sample changed from intergranular fractures to a mixture of intergranular and transgranular fractures. The sample underwent abrasive wear; however, the change in its wear performance was not significant. The results indicate that the material can be toughened without significant impact on hardness and wear resistance.
引用
收藏
页数:9
相关论文
共 50 条
  • [1] Microstructure development of WCoB-TiC based hard materials
    Sáez, A
    Arenas, F
    Vidal, E
    [J]. INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2003, 21 (1-2): : 13 - 18
  • [2] Effect of initial Co content on the microstructure, mechanical properties and high-temperature oxidation resistance of WCoB-TiC ceramic composites
    Ke, Deqing
    Pan, Yingjun
    Wu, Run
    Xu, Yuanyuan
    Wang, Pan
    Wu, Teng
    [J]. CERAMICS INTERNATIONAL, 2018, 44 (01) : 1213 - 1219
  • [3] Effect of NbC in-situ synthesis on the microstructure and properties of pre-placed WCoB-TiC coating by laser cladding
    Zhang, Hao
    Pan, Yingjun
    Zhang, Yang
    Lian, Guofu
    Cao, Qiang
    Zhu, Xingyu
    [J]. INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2022, 120 (1-2): : 1265 - 1280
  • [4] Effect of NbC in-situ synthesis on the microstructure and properties of pre-placed WCoB-TiC coating by laser cladding
    Hao Zhang
    Yingjun Pan
    Yang Zhang
    Guofu Lian
    Qiang Cao
    Xingyu Zhu
    [J]. The International Journal of Advanced Manufacturing Technology, 2022, 120 : 1265 - 1280
  • [5] Influence of laser power on the microstructure and properties of in-situ NbC/WCoB-TiC coating by laser cladding
    Zhang, Hao
    Pan, Yingjun
    Zhang, Yang
    Lian, Guofu
    Cao, Qiang
    Yang, Jianghuai
    [J]. MATERIALS CHEMISTRY AND PHYSICS, 2022, 290
  • [6] Effect of W/B atomic ratio on the microstructure and mechanical properties of WCoB-TiC ceramic composites: first-principles calculations and experiment
    Ke, Deqing
    Pan, Yingjun
    Wu, Teng
    Wang, Junkai
    Xu, Xin
    Pan, Yinghui
    [J]. JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2020, 9 (04): : 8744 - 8753
  • [7] Effect of sintering atmosphere on microstructure and properties of TiC based cermets
    周书助
    王社权
    王零森
    丁泽良
    [J]. Journal of Central South University, 2007, (02) : 206 - 209
  • [8] Effect of sintering atmosphere on microstructure and properties of TiC based cermets
    Shu-zhu Zhou
    She-quan Wang
    Lin-sen Wang
    Ze-liang Ding
    [J]. Journal of Central South University of Technology, 2007, 14 : 206 - 209
  • [9] Effect of Ni contents on the microstructure and mechanical properties of TiC-Ni cermets obtained by direct laser fabrication
    Li, Yuxin
    Bai, Pelikang
    Wang, Yaomin
    Hu, Jiandong
    Guo, Zuoxing
    [J]. INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2009, 27 (03): : 552 - 555
  • [10] Effect of sintering atmosphere on microstructure and properties of TiC based cermets
    Zhou Shu-zhu
    Wang She-quan
    Wang Lin-sen
    Ding Ze-liang
    [J]. JOURNAL OF CENTRAL SOUTH UNIVERSITY OF TECHNOLOGY, 2007, 14 (02): : 206 - 209