Long-Term Antifogging Coating Based on Black Phosphorus Hybrid Super-Hydrophilic Polymer Hetero-Network

The antifogging coating based on super-hydrophilic polymer is regarded as the most promising strategy to avoid fogging but suffers from short-term effectiveness due to antifogging failure induced by water invasion. In this study, a black phosphorus nanosheets (BPs) hybrid polymer hetero-network coating (PUA/PAHS/BPs HN) was prepared by UV curing for the first time to achieve long-term antifogging performance. The polymer hetero-network (HN) structure was composed of two novel cross-linked acrylic resin and polyurethane acrylate. Different from physical blending, a covalent P-C bond between BPs and polymer is generated by UV initiated free radical reaction, resulting in BPs firmly embedded in the polymer HN structure. The BPs enriched on the coating surface by UV regulating migration prevent permeation of water towards the inside of the coating through its own good water-based lubricity and water absorption capacity. Compared with the nonhybrid polymer HN, PUA/PAHS/BPs HN not only has higher hardness and better friction resistance properties, but also exhibits superior water resistance and longer antifogging duration. Since water invasion was greatly reduced by BPs, the PUA/PAHS/BPs HN coating maintained antifogging duration for 60 min under a 60 degrees C water vapor test and still maintained long-term antifogging performance after being immersed in water for 5 days.