Surface Modified CoCrFeNiMo High Entropy Alloys for Oxygen Evolution Reaction in Alkaline Seawater

Electrolysis of seawater is a promising technique to desalinate seawater and produce high-purity hydrogen production for freshwater and renewable energy, respectively. For the application of seawater electrolysis technique on a large scale, simplicity of manufacture method, repeatability of catalyst products, and stable product quality is generally required in the industry. In this work, a facile, one-step, and metal salt-free fabrication method was developed for the seawater-oxygen-evolution-active catalysts composed of CoCrFeNiMo layered double hydroxide array self-supported on CoCrFeNiMo high entropy alloy substrate. The obtained catalysts show improved performance for oxygen evolution reaction in alkaline artificial seawater solution. The best-performing sample delivered the current densities of 10, 50, and 100 mA cm(-2) at low overpotentials of 260.1, 294.3, and 308.4 mV, respectively. In addition, high stability is also achieved since no degradation was observed over the chronoamperometry test of 24 h at the overpotential corresponding to 100 mA cm(-2). Furthermore, a failure mechanism OER activity of multi-element LDHs catalysts was put forward in order to enhance catalytic performance and design catalysts with long-term durability.