New protective coatings against liquid zinc corrosion

被引：2
|
作者：
Cieplak, Aleksandra [1 ]
Gdoura, Asma [2 ]
Gay, Bruno [3 ]
Portebois, Leo [4 ]
Ramenatte, Nicolas [4 ]
Proriol Serre, Ingrid [1 ]
Balloy, David [1 ]
机构：
[1] Univ Lille, UMR 8207, CNRS, INRAE,UMET Unite Mat & Transformat,Cent Lille, F-59000 Lille, France
[2] Carthage Univ, Natl Inst Appl Sci & Technol INSAT, BP 676, Tunis 1080, Tunisia
[3] BCircle, 2 Clos 3 Couleurs, B-1150 Brussels, Belgium
[4] Univ Lorraine, EEIGM, 6 Rue Bastien Lepage, F-54010 Nancy, France
来源：
SN APPLIED SCIENCES | 2023年 / 5卷 / 05期
关键词：
Batch galvanizing; Molten zinc corrosion; Slurry process; WT.PERCENT B STEEL; INTERFACIAL MORPHOLOGY; STAINLESS-STEEL; AL SYSTEM; BEHAVIOR; RESISTANCE; ZN;
D O I：
10.1007/s42452-023-05319-6
中图分类号：
O [数理科学和化学]; P [天文学、地球科学]; Q [生物科学]; N [自然科学总论];
学科分类号：
07 ; 0710 ; 09 ;
摘要：
Hot dip galvanizing is a surface treatment used to form a corrosion-resistant layer on the surface of steel by dipping it in a liquid zinc bath. However, a lot of structures used for hanging or containing the parts during the process are made of steel and suffer from liquid zinc corrosion. Furthermore, Fe-Zn intermetallics formed on the surface induce an additional pickling and zinc consummation, therefore generating supplementary economic and environmental costs. In this article, two Fe-Cr-Ni-Si coatings synthetized by the slurry process on carbon steel (C22) were characterized by XRD, EDX, EPMA and EBSD analyses. Their corrosion protective properties were studied in the process imitating cyclic batch galvanizing and compared to those of uncoated carbon steel (C22) and stainless steel (316 L). The coatings were verified to be more efficient than the 316 L steel usually used for this application. After 9 cycles of no weight loss, molten zinc corrosion was linear and the same for Fe-Cr-Ni-Si coatings as for the stainless steel.
引用
收藏
页数：9
相关论文
共 50 条
  • [1] New protective coatings against liquid zinc corrosion
    Aleksandra Cieplak
    Asma Gdoura
    Bruno Gay
    Léo Portebois
    Nicolas Ramenatte
    Ingrid Proriol Serre
    David Balloy
    SN Applied Sciences, 2023, 5
  • [2] Silica sol - gel protective coatings against corrosion of zinc substrates
    Volentiru, Emoke
    Nyari, Maria
    Szabo, Gabriella
    Horvolgyi, Zoltan
    Muresan, Liana Maria
    PERIODICA POLYTECHNICA-CHEMICAL ENGINEERING, 2014, 58 : 61 - 66
  • [3] The 'liquid zinc' is new agent for protection against corrosion
    Labunskij, A.B.
    Mekhanizatsiya Stroitel'stva, 2004, (05): : 23 - 24
  • [4] Corrosion-protective properties of zinc coatings
    Yu. S. Gerasimenko
    M. V. Nechai
    N. A. Belousova
    Materials Science, 1999, 35 : 273 - 278
  • [5] Corrosion-protective properties of zinc coatings
    Gerasimenko, YS
    Nechai, MV
    Belousova, NA
    MATERIALS SCIENCE, 1999, 35 (02) : 273 - 278
  • [6] Accelerated Corrosion Tests for Protective Properties of Aluminum and Zinc Coatings
    Mat Sci, 6 (681):
  • [7] Investigation of the corrosion resistance of zinc-silicate protective coatings
    Aleksandrov, Yu.A.
    Shekunova, V.M.
    Yablokova, N.V.
    Biryukova, T.G.
    Beijing Keji Daxue Xuebao/Journal of University of Science and Technology Beijing, 1998, 20 (05):
  • [8] Investigation of the corrosion resistance of zinc-silicate protective coatings
    Aleksandrov, YA
    Shekunova, VM
    Yablokova, NV
    Biryukova, TG
    PROTECTION OF METALS, 1998, 34 (06): : 587 - 590
  • [9] Accelerated corrosion tests for protective properties of aluminum and zinc coatings
    Kwiatkowski, L
    Kwiecien, J
    Szustkiewicz, T
    MATERIALS SCIENCE, 1996, 32 (06) : 681 - 687
  • [10] ZINC POWDER COATINGS FOR PROTECTION OF STEEL AGAINST CORROSION
    OETEREN, KAV
    METALL, 1975, 29 (09): : 912 - 922
12345