Effect of dispersing agents on the electrical and mechanical performance of GNPs filled epoxy nanocomposite

In this work, graphene nanoplatelets (GNPs) filled epoxy nanocomposites with the addition of different dispersing agents were fabricated using a method combines mechanical mixing and tip sonication. The loading of GNPs used is 0.8 vol% determined previously as the amount required to achieve the percolation threshold to conduct electricity. Three dispersing agents were used in this work: Sodium dodecyl sulphate (SDS), ethanol and Phenyl glycidyl ether (PGE), with loadings varying from 2 vol% to 10 vol%. The incorporation of dispersing agent enhanced the electrical bulk conductivity of GNPs filled nanocomposites. The mechanical performance (flexural properties and fracture toughness) of the nanocomposite were evaluated and compared. The optimum loading of SDS to obtain the highest flexural strength and fracture toughness is 2 vol%, where further increases will deteriorate the performance of nanocomposites. On the other hand, the optimum loading of ethanol and PGE are 4 vol%. The fracture toughness of GNPs filled nanocomposites improved with the addition of 2 vol% SDS and deteriorated with increasing loadings of SDS up to 10 vol%. By incorporating 4 vol% of ethanol, the optimum fracture toughness of the nanocomposite is achieved. Fracture toughness is then dropped with further increases in ethanol. The addition of PGE caused deterioration in fracture toughness of GNPs filled epoxy nanocomposite.