Preparation of polysulfone/sulfonated polysulfone-SiO2 nanofiltration membrane and its performance characterization

Purpose - This study aims to optimize the preparation conditions and modify the nanofiltration (NF) membranes to prepare high-performance polysulfone/sulfonated polysulfone composite nanofiltration (PSF/SPSF-NF) membranes through interfacial polymerization.Design/methodology/approach- Investigating the impacts of anhydrous piperazine (PIP) concentration, trimesoyl chloride (TMC) concentration and basement membrane type on NF membrane performance, the optimal membrane was prepared. In addition, nano-SiO2 was added to the active separation layer to modify the NF membranes.Findings- The comprehensive performance of PSF/SPSF-NF membranes was optimized when the concentration of PIP was 0.75 Wt.% and the concentration of TMC was 0.15 Wt.%, at which time the water flux was 66.1 L center dot m(-2)center dot h(-1 )and the retention rate of Na2SO4 was 98.1%. The comprehensive performance of polysulfone/sulfonated polysulfone-SiO2 nanofiltration (PSF/SPSF-SiO2-NF) membranes was optimized when the blending ratio of nano-SiO2 to PIP was 2:3, with a pure water flux of 81.9 L center dot m(-2)center dot;h(-1) and a Na2SO4 retention rate of 95.9%. Compared to polysulfone nanofiltration (PSF-NF) membranes and PSF/SPSF-NF membranes, NF membranes with nano-SiO2 increased the flux recovery rate by 22.9% and 8.7%.Practical implications- PSF/SPSF-SiO2-NF membrane exhibits excellent antifouling properties.Originality/value- There is currently no literature available on the preparation of NF membranes using polysulfone/sulfonated polysulfone (PSF/SPFS) as a substrate. This provides a method for modifying NF membranes, starting with the modification of the basement membrane and then modifying the active separation layer.