Effectiveness of surface treatment on bond strength of ceramic brackets to two types of CAD/CAM-prepared nanohybrid composites

Objectives The aim of this study was to assess the influence of surface treatment on the shear bond strength of two different adhesive-coated orthodontic ceramic brackets to computer-aided design/computer-aided manufacturing (CAD/CAM) nanohybrid composite. Methods A total of 120 specimens (10 mm x 10 mm x 3 mm) were prepared from each type of CAD/CAM block (Grandio [GR], VOCO Cuxhaven, Germany; Lava Ultimate [LU], 3M ESPE, St. Paul, MN, USA). For each type of CAD/CAM block, the plates were divided into four groups based on the applied surface treatment: hydrofluoric acid (HF), grinding bur (GB), silica coating with CoJet system (CS), and titanium tetrafluoride (TiF4) 2 wt/v%. Maxillary central incisors of adhesive-coated ceramic orthodontic brackets (APC Flash-free Clarity Advanced Ceramic, 3M Unitek, Monrovia, CA, USA) were bonded using Transbond XT Primer (3M Unitek, Monrovia, CA, USA). Shear bond strength was conducted, and the modes of failure were assessed utilizing the adhesive remnant index. Surface roughness and topography of treated CAD/CAM were evaluated. Data were statistically analyzed using two-way analysis of variance (ANOVA) and Tukey's test. The Weibull analysis was conducted on shear bond strength data. Results Surface treatment with 2% TiF4 wt/v revealed significantly higher bond strength (GR, 14.51 +/- 2.57 MPa; LU, 11.19 +/- 2.17 MPa) than other groups for both types of CAD/CAM restorative materials (p < 0.05). Adhesive failures were the predominant mode of failure. Surface treatment with CS revealed higher surface roughness than other groups (p < 0.05). Conclusions Surface treatment with 2% TiF4 wt/v enhanced the adhesion between orthodontic ceramic brackets to GR and LU CAD/CAM composite restorative materials. GR CAD/CAM nanohybrid composite had higher bond strength than LU to ceramic orthodontic brackets.