Corrosion by a Heavy Metal Oxide Glass

Melts of lead bismuth gallate compositions are highly corrosive and attack on crucibles of different materials. In the present study, corrosion by a base glass (50PbO-30Bi2O3-20Ga2O3 in mole fraction) melted using different crucibles and the effect on UV-VIS and IR edges were studied. By melting the base glass in platinum/2% rhodium, gold zirconia and alumina crucibles showed less effect on the IR edge and therefore shifted the infrared edge to longer wavelength, whereas silica crucible contaminated the glass, causing a severe deterioration in the infrared and hence shifted infrared edge to much shorter wavelength. In the UV-VIS region, base glass melted in platinum/2% rhodium crucible shifted the edge to the longest wavelength whereas silica crucible shifted the edge to shorter wavelength. The contaminants from gold, zirconia and alumina crucibles caused the UV-VIS edge of the base glass to lie between the two extremes of Pt/2% Rh and SiO2 crucibles. The glasses melted in above mentioned crucibles were