Electrochemical corrosion behavior of carbon steel with bulk coating holidays

被引：0
|
作者：
Yiquan Song1
机构：
来源：
International Journal of Minerals,Metallurgy and Materials | 2006年 / 01期
关键词：
bulk coating holidays; EIS; cathodic protection (CP); crevice corrosion;
D O I：
暂无
中图分类号：
TG174.44 [金属复层保护];
学科分类号：
080503 ;
摘要：
With epoxy coal tar as the coating material, the electrochemical corrosion behavior of Q235 with different kinds of bulk coating holidays has been investigated with EIS (Electrochemical Impedance Spectroscopy) in a 3.5vol％ NaCl aqueous solution. The area ratio of bulk coating holiday to total coating area of steel is 4.91％. The experimental results showed that at free corrosion potential, the corrosion of carbon steel with disbonded coating holiday is heavier than that with broken holiday and disbonded & broken holiday with time; Moreover, the effectiveness of Cathodic Protection (CP) of carbon steel with broken holiday is better than that with disbonded holiday and disbonded & broken holiday on CP potential-850 mV (vs CSE). Further analysis indicated that the two main reasons for corrosion are electrolyte solution slowly penetrating the coating, and crevice corrosion at steel/coating interface near holidays. The ratio of impedance amplitude (Z) of different frequency to minimum frequency is defined as K value. The change rate of K with frequency is related to the type of coating holiday.
引用
收藏
页码：37 / 43
页数：7
相关论文
共 50 条
  • [1] Electrochemical corrosion behavior of carbon steel with bulk coating holidays
    Song, YQ
    Du, CW
    Li, XG
    [J]. JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING, 2006, 13 (01): : 37 - 43
  • [2] Corrosion electrochemical behavior of Zn-Al silane coating on carbon steel
    Zhou Wenjuan
    Xu Likun
    Wang Jia
    Li Ning
    Xue Lili
    Chen Guangzhang
    [J]. ACTA METALLURGICA SINICA, 2007, 43 (09) : 983 - 988
  • [3] Electrochemical corrosion behavior of nanocrystallized bulk 304 stainless steel
    Li, Nan
    Li, Ying
    Wang, Shenggang
    Wang, Fuhui
    [J]. ELECTROCHIMICA ACTA, 2006, 52 (03) : 760 - 765
  • [4] Electrochemical and corrosion behavior of carbon steel in SULFIRAN® process
    Neshati, J.
    Abedi, S. Sh.
    Forsat, Kh.
    Jenab, M. Hosseini
    Mirfendereski, S.
    [J]. MATERIALS SCIENCE AND ENGINEERING B-ADVANCED FUNCTIONAL SOLID-STATE MATERIALS, 2009, 162 (01): : 40 - 46
  • [5] Electrochemical corrosion behavior of carbon steel in marine microbial medium
    College of Materials Science and Technology, Shandong University, Jinan 250061, China
    不详
    [J]. Huagong Xiandai, 2006, SUPPL. 2 (281-284):
  • [6] THE ELECTROCHEMICAL BEHAVIOR OF OCEANIC MICROBIOLOGICAL INFLUENCED CORROSION ON CARBON STEEL
    X.T. Chang1
    [J]. Acta Metallurgica Sinica(English Letters), 2007, (05) : 334 - 340
  • [7] Wear and Corrosion Behavior of Tungsten Carbide Based Coating on Carbon Steel
    Ahmad, Noor Aqilah
    Kamdi, Zakiah
    Tobi, Abdul Latif Mohd
    [J]. INTERNATIONAL JOURNAL OF INTEGRATED ENGINEERING, 2018, 10 (04): : 119 - 125
  • [8] Electrochemical Corrosion Behavior of Thermally Sprayed Nichrome Coating on Duplex Stainless Steel
    Kuruvila, Roshan
    Sundaresan, Thirumalai Kumaran
    Ahmed, Farooq
    Marimuthu, Uthayakumar
    [J]. JOURNAL OF TESTING AND EVALUATION, 2024, 52 (01) : 203 - 217
  • [9] Electrochemical Corrosion Behavior of Thermally Sprayed Nichrome Coating on Duplex Stainless Steel
    Kuruvila, Roshan
    Sundaresan, Thirumalai Kumaran
    Ahmed, Farooq
    Marimuthu, Uthayakumar
    [J]. JOURNAL OF TESTING AND EVALUATION, 2023,
  • [10] Electrochemical preparation and corrosion resistance of conductive PEDOT coating on carbon steel surface
    Gao, Bo-Wen
    Wang, Mei-Han
    Yan, Mao-Cheng
    Lei, Hao
    [J]. Surface Technology, 2020, 49 (09): : 298 - 305
12345