Investigation of tribological characteristics of nickel alloybased solid-lubricating composites at elevated temperatures under vacuum

The development of a high-performance solid-lubricating composite with excellent self-lubricity over a broad temperature range in vacuum is significant to solve the frictional problems of spatial mechanisms. In this study, the vacuum tribological behaviors of nickel-matrix/Ag/(Ca, Ba)F2/graphite(0–2 wt%) composites were studied from 25 to 800 °C. The results show that the synergistic effects of solid lubricants can significantly improve the tribological properties of the composites in vacuum, with the graphite content contributing considerably. For 2 wt% graphite, a low friction coefficient(0.14–0.25) and the lowest wear rate((0.12–4.78)×10-5mm~3·N-1·m-1) were observed in vacuum over the entire testing temperature range. Moreover, the wear mechanisms were clarified via analysis of the chemical composition and morphologies of the sliding surfaces.