Pseudoelasticity and elastocaloric effect of Fe75.5Ga24.5 single crystal

<100>-,<112>-and <149>-oriented single crystals of Fe75.5Ga24.5alloy were prepared by optical float zone melting method.The pseudoelasticity behavior and elastocaloric effect of the single crystals were investigated,as well as the associate microstructures.D03phase structure was realized by solution treatment at 800 0C and annealed at 600℃ for 10 h.The compressive deformation behavior exhibits significant dependence on the crystalline directions.Excellent pseudoelasticity with recoverable strain up to 5% is obtained by compression along <149>direction.The pseudoelasticity disappears after five deformation cycles.Adiabatic temperature change is simultaneously detected during the pseudoelasticity,especially during loading process.