EFFECTS OF STRESS RATIO AND FREQUENCY ON CORROSION FATIGUE CRACK GROWTH MECHANISM IN LOW ALLOY STEELS

被引：0

作者：

HAN Enhou HAN KYumei ZHENG Yuli KE Wei Corrosion Science Laboratory

机构：

来源：

Acta Metallurgica Sinica(English Letters) | 1993年 / 06期

关键词：

corrosion fatigue; stress ratio; crack growth; electrode potential; steel ZG20SiMn; steel SM50B-Zc;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Based on theoretical analysis about local strain,strain rate and dissolving rate at crack tip,the corrosion fatigue crack growth rate of steels ZG20SiMn and SM50B-Zc in fresh waterand 3.5% NaCl solution were measured experimentally,and the PH and electrode potentialwithin crack were also measured continuously along with crack propagating.It showed thatthe increase of crack growth rate,caused by both decreasing frequency and raising stressratio,was mainly accelerated by hydrogen embrittlement.

引用

页码：373 / 378

页数：6

共 50 条

[1] Effects of stress ratio and frequency on corrosion fatigue crack growth mechanism in low alloy steels
Han, Enhou
Han, Kyumei
Zheng, Yuli
Ke, Wei
Acta Metallurgica Sinica Series A, Physical Metallurgy & Materials Science, 1993, 6 A (06): : 373 - 378
[2] Surface-crack aspect ratio development during corrosion-fatigue crack growth in low-alloy steels
James, LA
NUCLEAR ENGINEERING AND DESIGN, 1997, 172 (1-2) : 61 - 71
[3] Fatigue Crack Initiation and Growth of Aluminum Alloy with Stress Ratio Effects
Haftirman, Idrus
Afendi, M.
Hoe, Wong Chun
ADVANCED MATERIALS ENGINEERING AND TECHNOLOGY II, 2014, 594-595 : 1105 - 1111
[4] THE INFLUENCE OF ENVIRONMENT AND STRESS RATIO ON FATIGUE CRACK-GROWTH AT NEAR THRESHOLD STRESS INTENSITIES IN LOW-ALLOY STEELS
STEWART, AT
ENGINEERING FRACTURE MECHANICS, 1980, 13 (03) : 463 - +
[5] EFFECT OF STRESS RATIO AND FREQUENCY ON FATIGUE CRACK GROWTH
MUSUVA, JK
RADON, JC
FATIGUE OF ENGINEERING MATERIALS AND STRUCTURES, 1979, 1 (04): : 457 - 470
[6] EFFECTS OF STRESS RATIO ON CORROSION FATIGUE CRACK GROWTH OF A HIGH STRENGTH STEEL.
Huang, Shuju
Zhang, Pingsheng
Quan, Gaofeng
Song, Yujiu
Key Engineering Materials, 1987, 20-28 (pt 1-4)
[7] Waveform and frequency effects on corrosion-fatigue crack growth behaviour in modern marine steels
Igwemezie, Victor
Mehmanparast, Ali
INTERNATIONAL JOURNAL OF FATIGUE, 2020, 134
[8] EFFECT OF STRESS RATIO ON FATIGUE CRACK GROWTH-RATES IN STEELS
VOSIKOVSKY, O
ENGINEERING FRACTURE MECHANICS, 1979, 11 (03) : 595 - 602
[9] Evaluation of the mitigation effect of hydrogen water chemistry in BWRs on the low-frequency corrosion fatigue crack growth in low-alloy steels
Ritter, S.
Seifert, H. P.
JOURNAL OF NUCLEAR MATERIALS, 2007, 360 (02) : 170 - 176
[10] Effect of Microstructure on the Corrosion Fatigue Crack Growth of Low and Medium Steels
Wang, Jing
Zhang, Yan
Yu, Chunting
Zhao, Bo
ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, 2022, 2022

← 1 2 3 4 5 →