Effects of overaging temperature on the microstructure and properties of 600MPa cold-rolled dual-phase steel

C–Mn steels prepared by annealing at 800°C for 120 s and overaging at 250–400°C were subjected to pre-straining（2%） and baking treatments（170°C for 20 min） to measure their bake-hardening（BH;） values. The effects of overaging temperature on the microstructure, mechanical properties, and BH;behavior of 600 MPa cold-rolled dual-phase（DP） steel were investigated by optical microscopy, scanning electron microscopy, and tensile tests. The results indicated that the martensite morphology exhibited less variation when the DP steel was overaged at 250–350°C. However, when the DP steel was overaged at 400°C, numerous non-martensite and carbide particles formed and yield-point elongation was observed in the tensile curve. When the overaging temperature was increased from 250 to 400°C, the yield strength increased from 272 to 317 MPa, the tensile strength decreased from 643 to 574 MPa, and the elongation increased from 27.8% to 30.6%. Furthermore, with an increase in overaging temperature from 250 to 400°C, the BH;value initially increases and then decreases. The maximum BH;value of 83 MPa was observed for the specimen overaged at 350°C.