Study on Characteristics and Generation Mechanism of YAG Pulsed Laser Welding Cracks of AZ31B Magnesium Alloy

被引：0
|
作者：
Cui ZeqinWang WenxianSi EnXu BingsheKey Laboratory of Interface Science and Engineering in Advanced Materials Taiyuan University of TechnologyMinistry of EducationTaiyuan ChinaCollege of Materials Science and EngineeringTaiyuan University of TechnologyTaiyuan China [1 ,2 ,1 ,2 ,1 ,1 ,21 ,30024 ,2 ,30024 ]
机构：
来源：
稀有金属材料与工程 | 2011年 / 40(S4)卷 / S4期
关键词：
AZ31B magnesium alloy; Nd:YAG pulsed laser; laser welding; welding crack; crack extension;
D O I：
暂无
中图分类号：
TG456.7 [激光焊];
学科分类号：
摘要：
Due to poor metallurgical weldability of magnesium alloy,laser welding crack is still one of the main defects.The generations of welding crack seriously affected the weld quality and reduce the mechanical properties of welded joints which have become a bottleneck of the magnesium alloy products widely used in the structure materials.In this paper,AZ31B magnesium alloy sheet with 2mm thickness was used for this investigation.The forming reason and extending characteristics of the welding cracks were investigated during the Nd:YAG pulsed laser welding.The results show that welding cracks are mainly solidification crack which were always present in the weld centers.Few welding hot cracks appear multiple furcation phenomenons,and main and branch cracks were intercrystalline crack.The partial branch crack was mixed intercrystalline and transgranular extension.In addition,few cracks in the weld were caused due to irregular shape porosity and inclusion.The delayed crack weren't observed in the weld after deposited 48 hours.In the pre-process on the basis,the characteristics and generation mechanism of YAG pulsed laser welding cracks of magnesium alloy were analyzed further.
引用
收藏
页码：21 / 25
页数：5
相关论文
共 12 条
  • [1] Quan Y J,Chen Z H,Gong X S et al. Materials Characteriza-tion . 2008
  • [2] S Riekehr,M Ko ak,A R Pyzalla. Materials Science and En-gineering A . 2008
  • [3] Electron-beam welding behavior in Mg-Al based alloys. Su S F, Huang J C, Lin H K, et al. Metallurgical and Materials Transactions A Physical Metallurgy and Materials Science . 2002
  • [4] Neural-fuzzy fault diagnosis in a marine propulsion shaft system. Kuo Hsing Chia, Wu Li Jen, Chen Jun Hom. Journal of Materials . 2002
  • [5] Hybrid laser-TIG welding, laser beam welding and gas tungsten arc welding of AZ31B magnesium alloy. Liu Liming, Wang Jifeng, Song Gang. Journal of Materials Science . 2004
  • [6] Mechanical properties and microstructure of gas tungsten arc welded magnesium AZ91D plates. Munitz A, Cotler C, Stern A, et al. Materials Science and Engineering A: Structural Materials:Properties, Microstructure and Processing . 2001
  • [7] Light-weight structures produced by laser beam joining for future applications in automobile and aerospace industry. Schubert E, Klassen M, Zerner I, et al. Journal of Materials . 2001
  • [8] X Cao,M Jahazi,J P Immarigeon et al. Journal of Materials . 2006
  • [9] Zhu Jinhong,Li Lin,Liu Zhu. Applied Surface Science . 2005
  • [10] L K Pan,C C Wang,Y C Hsiao et al. Optics and Laser Tech-nology . 2004
12