Hot deformation behavior of Cu-bearing antibacterial titanium alloy

We investigated the deformation behavior of a new biomedical Cu-bearing titanium alloy(Ti-645（Ti-6.06 A1-3.75 V-4.85 Cu, in wt%）) to optimize its microstructure control and the hot-working process. The results showed that true stress-true strain curve of Ti-645 alloy was susceptible to both deformation temperature and strain rate. The microstructure of Ti-645 alloy was significantly changed from equiaxed grain to acicular one with the deformation temperature while a notable decrease in grain size was recorded as well. Dynamic recovery（DRV） and dynamic recrystallization（DRX） obviously existed during the thermal compression of Ti-645 alloy. The apparent activation energies in（α+β） phase and β single phase regions were calculated to be 495.21 kJ mol;and 195.69 kJ mol;, respectively. The processing map showed that the alloy had a large hot-working region whereas the optimum window occurred in the strain rate range of 0.001-0.1 s;, and temperature range of 900-960℃ and 1000-1050℃. The obtained results could provide a technological basis for the design of hot working procedure of Ti-645 alloy to optimize the material design and widen the potential application of Ti-645 alloy in clinic.