Effect of Alloyed Mo on Mechanical Properties,Biocorrosion and Cytocompatibility of As-Cast Mg-Zn-Y-Mn Alloys

The influences of Mo contents on mechanical properties,biocorrosion and cytocompatibility of as-cast Mg-6Zn-8.16Y-2.02Mn-xMo(x=0.0,0.1,0.3,0.5,0.7 wt%) alloys were firstly investigated.Appropriate amount of Mo was conducive to grain refinement and the formation of long-period stacking ordered structure with continuous distribution,which was advantageous to mechanical properties and corrosion resistance.Mg-6Zn-8.16Y-2.02Mn-0.3Mo exhibited the ultimate tensile strength of 265.0 MPa,elongation of 13.5% and the lowest weight loss rate in Hank’s solution.Moreover,the cell toxicity cultured in 25% extract was evaluated and the alloy with 0.3 wt% Mo exhibited the best cytocompatibility.Thus,the alloy was expected to become a novel biodegradable implant material.