HIGH SOLIDS-CONTENT NANOSIZE POLYMER LATEXES MADE BY A MODIFIED EMULSION COPOLYMERIZATION

被引：0
|
作者：
ZHANG Yuying [345 ]
机构：
来源：
ChineseJournalofReactivePolymers | 2003年 / 01期
关键词：
Microemulsion; Nanosize polymer latexes; Acrylate;
D O I：
暂无
中图分类号：
TQ316.3 [聚合反应过程];
学科分类号：
0805 ; 080502 ;
摘要：
Polymer nanoparticles were prepared in the methyl methacrylate (MMA)/butyl methacrylate (BA) emulsion copolymerization process by a modified microemulsion copolymerization method. 2-Hydroxyethyl methacrylate(HEMA), acrylate (AA) and methyl acrylate (MAA) were used as reactive cosurfactants. With this process high polymer: surfactant weight ratios (40:1 or greater), relatively concentrated (~30wt. %) latexes and small (~60nm) particle diameters were obtained. Properties of the latexes were characterized by TEM, DSC, dynamic light scattering, and IR spectroscopy.
引用
收藏
页码：10 / 16
页数：7
相关论文
共 50 条
  • [1] High solids-content nanosize polymer latexes made by microemulsion polymerization
    Ming, W
    Jones, FN
    Fu, SK
    MACROMOLECULAR CHEMISTRY AND PHYSICS, 1998, 199 (06) : 1075 - 1079
  • [2] High solids-content nanosize polymeric microlatexes made by microemulsion copolymerization at ambient temperature
    Ke Chang-mei
    Wang Hou-zhi
    Deng Wei
    Wang Yan
    Xu Jun
    Duan Hui
    Zhang Mei-jie
    Zhao Hui-zhong
    Li Xuan-ke
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2004, 19 (1): : 30 - 33
  • [3] High Solids-Content Nanosize Polymeric Microlatexes Made by Microemulsion Copolymerization at Ambient Temperature
    柯昌美
    Journal of Wuhan University of Technology-Materials Science, 2004, (01) : 30 - 33
  • [4] High solids-content nanosize polymeric microlatexes made by microemulsion copolymerization at ambient temperature
    Ke, CM
    Wang, HZ
    Deng, W
    Wang, Y
    Xu, J
    Duan, H
    Mang, MJ
    Zhao, HZ
    Li, XK
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2004, 19 (01): : 30 - +
  • [5] Water-borne coatings formulated from high solids-content nanosize polymeric microlatexes.
    Ming, WH
    Zhao, YQ
    Fu, SK
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1999, 217 : U478 - U478
  • [6] Semi-batch emulsion copolymerization of styrene and butyl acrylate for production of high solids content latexes: Experiments and mathematical model
    Marinangelo, Giovane
    Hirota, Wilson H.
    Giudici, Reinaldo
    CHEMICAL ENGINEERING SCIENCE, 2011, 66 (23) : 5875 - 5890
  • [7] Nanosize polymer latices made by microemulsion copolymerization: Preparation and characterization
    Zhang, YY
    Guo, TY
    Hao, GJ
    Song, MD
    Zhang, BH
    JOURNAL OF APPLIED POLYMER SCIENCE, 2003, 90 (13) : 3625 - 3630
  • [8] Increasing Starch Nanoparticle Content in Emulsion Polymer Latexes
    Zhang, Yujie
    Cunningham, Michael F.
    Smeets, Niels M. B.
    Dube, Marc A.
    INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH, 2019, 58 (46) : 20987 - 20995
  • [9] High solids content latexes with low viscosity
    F. Chu
    A. Guyot
    Colloid and Polymer Science, 2001, 279 : 361 - 367
  • [10] High solids content latexes with low viscosity
    Chu, F
    Guyot, A
    COLLOID AND POLYMER SCIENCE, 2001, 279 (04) : 361 - 367
12345