Fabrication and Characterization of VO2 Thin Films by Direct Current Facing Targets Magnetron Sputtering and Low Temperature Oxidation

Low valence vanadium oxide(VO2-x) thin films were prepared on SiO2/Si substrates at room temperature by direct current facing targets reactive magnetron sputtering, and then proc- essed through rapid thermal annealing. The effects of the annealing on the structure and phase transition property of VO2 were discussed. X-ray photoelectron spectroscopy, X-ray diffraction tech- nique and Fourier transform infrared spectroscopy were employed to study the phase composition and structure of the thin films. The resistance-temperature property was measured. The results show that VO2 thin film is obtained after annealed at 320 ℃ for 3 h, its phase transition tempera- ture is 56 ℃, and the resistance changes by more than 2 orders. The vanadium oxide thin films are applicable in thermochromic smart windows, and the deposition and annealing process is compatible with micro electromechanical system process.