Microscopic phase-field simulation of Cr atom substitution character during formation of L12 and DO22 phases in Ni-Cr-Al alloy

The simulations of Cr atom substitution character during the formation of L12 and DO22 phases in Ni-Cr-Al alloy were performed at 873 K based on microscopic phase-field model. It is found that the substitution of Cr is affected by Cr and Al contents and limits of occupation probabilities of Cr atom in L12 phase are present. The precipitate is single L12 phase when the component is less than the limit, Cr atoms substitute the Al sublattices in L12 phase, and both of atoms Al and Cr occupy the β-sites and complex phases Ni3(Al1?xCrx) are formed; Cr atoms enter Ni sites when Al and Cr contents exceed the limit, and substitute β-sites or both of α- and β-sites. The DO22 phase is formed at the boundary of L12 phase.