Friction and Wear Behavior of Resin/Graphite Composite under Dry Sliding

被引：0
|
作者：
Zhenguo Zhu [1 ]
Shuo Bai [1 ]
Junfeng Wu [1 ]
Li Xu [1 ]
Ting Li [1 ]
Yong Ren [1 ]
Chang Liu [1 ]
机构：
[1] Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences
来源：
Journal of Materials Science & Technology | 2015年 / 31卷 / 03期
关键词：
Resin/graphite composite Friction and wear "Dusting" wear Transfer film;
D O I：
暂无
中图分类号：
TB33 [复合材料];
学科分类号：
0805 ; 080502 ;
摘要：
The friction and wear behavior of resin/graphite composite has been investigated using a pin-on-disc configuration under dry sliding condition. The results showed that the resin/graphite composite exhibited much better mechanical and tribological properties compared with the unimpregnated graphite. The friction coefficient was reduced by addition of furan resin, which could also prevent the"dusting" wear at loads more than 15 MPa. The steady and lubricated transfer film was easily formed on the counterpart surface due to the interaction of furan resin and wear debris of graphite, which was useful to reduce the wear rate of the resin/graphite composite. The composite is highly promising for mechanical sealing application and can be used at high load for long time sliding.
引用
收藏
页码：325 / 330
页数：6
相关论文
共 50 条
  • [1] Friction and Wear Behavior of Resin/Graphite Composite under Dry Sliding
    Zhu, Zhenguo
    Bai, Shuo
    Wu, Junfeng
    Xu, Li
    Li, Ting
    Ren, Yong
    Liu, Chang
    [J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2015, 31 (03) : 325 - 330
  • [2] On dry sliding friction and wear behavior of PPESK filled with PTFE and graphite
    Zhang, Xintao
    Liao, Gongxiong
    Jin, Qifeng
    Feng, Xuebin
    Jian, Xigao
    [J]. TRIBOLOGY INTERNATIONAL, 2008, 41 (03) : 195 - 201
  • [3] Research on Wear Behavior of Different Graphite Contents of NBR Under Dry Sliding
    Yang, Fengyan
    Sun, Yingnan
    Wang, Shijie
    [J]. PROCEEDINGS OF 2013 INTERNATIONAL CONFERENCE ON QUALITY, RELIABILITY, RISK, MAINTENANCE, AND SAFETY ENGINEERING (QR2MSE), VOLS I-IV, 2013, : 1037 - 1039
  • [4] The Effect of Load on Friction and Wear Behavior of NBR and FPM under Dry Sliding
    Lv, Xiaoren
    Sun, Hao
    Luo, Xuan
    Wang, Shijie
    [J]. ADVANCED MATERIALS, PTS 1-4, 2011, 239-242 : 985 - 989
  • [5] Wear and Friction Behavior of Epoxy/MWCNTs Nanocomposites under Dry Sliding Conditions
    Sabarinathan, C.
    Ali, Md Naushad
    Muthu, S.
    [J]. CURRENT NANOSCIENCE, 2013, 9 (06) : 766 - 772
  • [6] Dry Sliding Wear Behavior of Cu-Graphite Composite within a Wide Range of Sliding Velocity
    Ma, Wenlin
    Lu, Jinjun
    [J]. ADVANCED TRIBOLOGY, 2009, : 404 - 405
  • [7] Stastical Analysis of Dry Sliding Wear and Friction Behavior of Cu/SiC Sintered Composite
    Somani, Nalin
    Gautam, Yash Kumar
    Sharma, Sunil Kumar
    Kumar, Monu
    [J]. PROCEEDINGS OF THE 1ST INTERNATIONAL CONFERENCE ON MECHANICAL AND MATERIALS SCIENCE ENGINEERING: INNOVATION AND RESEARCH-2018 (ICMMSE:IR 2018), 2018, 2018
  • [8] Friction and wear behavior of surface nanocrystallized aluminium alloy under dry sliding condition
    Prakash, N. Arun
    Gnanamoorthy, R.
    Kamaraj, M.
    [J]. MATERIALS SCIENCE AND ENGINEERING B-ADVANCED FUNCTIONAL SOLID-STATE MATERIALS, 2010, 168 (1-3): : 176 - 181
  • [9] Wear mechanism of Al-Si alloy impregnated graphite composite under dry sliding
    Goto, H
    Uchijo, K
    [J]. WEAR, 2005, 259 (1-6) : 613 - 619
  • [10] Friction and wear behavior of copper-graphite composite material in high-speed sliding with current
    Du Sanming
    Zhao Fei
    Zhang Yongzhen
    [J]. EMERGING MATERIALS AND MECHANICS APPLICATIONS, 2012, 487 : 411 - 415
12345