Superplasticity and superplastic instability of AZ31B magnesium alloy sheet

被引：1
|
作者：
汪凌云 [1 ]
宋美娟 [2 ]
刘饶川 [3 ]
机构：
[1] College of Materials Science and Engineering, Chongqing University Chongqing 400044, China
[2] College of Materials Science and Engineering, Chongqing University Chongqing 400044, China Department of Mechanical Engineering, Chongqing University of Science and Technology, Chongqing 400050, China
[3] Department of Mechanical Engineering, Chongqing University of Science and Technology Chongqing 400050, China
来源：
Transactions of Nonferrous Metals Society of China | 2006年 / 02期
关键词：
AZ31B magnesium alloy; superplasticity; superplastic instability; strain sensitivity; cavity evolution; damage;
D O I：
暂无
中图分类号：
TG113.253 [];
学科分类号：
摘要：
Superplastic deformation mechanism of AZ31B magnesium alloy sheet was investigated. Maximum elongation of 216% and strain rate sensitivity of 0.36 were obtained at 723 K and a strain rate of 1×10?3s?1. It is found that dynamic recrystallization occurs at the early deformation stage, and that grain boundary sliding is the dominant deformation mode of superplastic AZ31B sheet, whose fracture is due to the growth and interlinkage of cavities nucleated at grain boundary. A cavity growth model was established, and damage characteristic parameters as well as the critical value of damage variable were identified so as to provide a theoretical ground on which the plastic forming technology of magnesium alloy sheet can be optimized.
引用
收藏
页码：327 / 332
页数：6
相关论文
共 50 条
  • [1] Superplasticity and superplastic instability of AZ31B magnesium alloy sheet
    Wang, LY
    Song, MJ
    Liu, RC
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2006, 16 (02) : 327 - 332
  • [2] Superplastic forming limit and instability of AZ31B sheet
    Song Meijuan
    Wang Lingyun
    Liu Raochuan
    ADVANCED STRUCTURAL MATERIALS, 2011, 686 : 343 - +
  • [3] Superplastic forming limit and instability of AZ31B sheet
    Wang, Lingyun
    Song, Meijuan
    Liu, Raochuan
    2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM, 2007, 546-549 : 387 - +
  • [4] Superplastic Gas Bulging Forming of AZ31B Magnesium Alloy Thin Sheet
    Zhang Qinglai
    Xiao Fugui
    Guo Hailing
    Bondarev, A. B.
    Bondarev, B. I.
    RARE METAL MATERIALS AND ENGINEERING, 2009, 38 (07) : 1259 - 1263
  • [5] Superplastic forming behaviors and microstructure characters of magnesium alloy sheet AZ31B
    Jin, QL
    Wu, HY
    MATERIALS PROCESSING AND DESIGN: MODELING, SIMULATION AND APPLICATIONS, PTS 1 AND 2, 2004, 712 : 1682 - 1686
  • [6] Brazing of AZ31B magnesium alloy sheet
    Watanabe, Takehiko
    Oohara, Kengo
    THERMEC 2006, PTS 1-5, 2007, 539-543 : 1603 - +
  • [7] Formability of AZ31B magnesium alloy sheet
    Wang L.
    Lu Z.
    Zhao Y.
    Qiu X.
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2006, 21 (2): : 25 - 27
  • [8] The Formablity of AZ31B Magnesium Alloy Sheet
    汪凌云
    卢志文
    Journal of Wuhan University of Technology(Materials Science Edition), 2006, (02) : 25 - 27
  • [9] The formablity of AZ31B magnesium alloy sheet
    Wang Lingyun
    Lu Zhiwen
    Zhao Yazhong
    Qiu Xiaogang
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2006, 21 (02): : 25 - 27
  • [10] Superplastic Behavior and Constitutive Equation of AZ31B Magnesium Alloy
    Chen, Fuxiao
    Chen, Xiangzhen
    Sun, Futao
    MATERIALS AND COMPUTATIONAL MECHANICS, PTS 1-3, 2012, 117-119 : 1689 - +
12345