Degradation characteristics of Ti/(IrO2+Ta2O5) coating anodes in H2SO4 solution

被引:0
|
作者
胡吉明
吴继勋
孟惠民
孙冬柏
朱艳冗
杨德钧
机构
关键词
oxide anodes; iridium oxide; tantalum oxide; degradation;
D O I
暂无
中图分类号
TG154.5 [涂镀材料];
学科分类号
摘要
The service life of Ti based IrO 2+Ta 2O 5 coating anodes over the whole composition range and prepared at different temperatures was studied by the accelerated electrolysis tests. The results show that as a result of incompleted decomposition, coatings obtained at low temperature are not stable. At the preparing temperature up to 450 ℃,the stability of the resulting deposits increase dramatically, and is independent on temperature. However, at higher temperature, oxidation of Ti base occurred leading to a decrease in the adhesion of coatings which resulted in decreasing of the service life of anodes. The maximum durability was obtained for the anodes prepared at 450 ℃.Resulting from the maximum solubility between the iridium and tantalum oxides, coatings with 70%IrO 2+30%Ta 2O 5 (mole fraction) exhibited the maximum stability. A preferential dissolution of Ir on the non close packed planes of the rutile oxides was observed for the pure IrO 2 deposits while on the close packed planes for the IrO 2 and Ta 2O 5 mixed ones in electrolysis. This dissolution characteristic can interpret a low service life for the coating anodes with a low IrO 2 content since the close packed planes orientations are dominant in these flesh samples. Two mechanisms for the degradation of Ti/(IrO 2+Ta 2O 5) anodes were also proposed.
引用
收藏
页码:511 / 515
页数:5
相关论文
共 50 条
  • [1] Degradation characteristics of Ti/(IrO2+Ta2O5) coating anodes in H2SO4 solution
    Hu, JM
    Wu, JX
    Meng, HM
    Sun, DB
    Zhu, YR
    Yang, DJ
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2000, 10 (04) : 511 - 515
  • [2] Ti基IrO2+Ta2O5阳极在H2SO4溶液中的电解时效行为
    胡吉明
    孟惠民
    张鉴清
    曹楚南
    物理化学学报, 2002, (01) : 14 - 20
  • [4] Improvement of stability of trivalent chromium electroplating of Ti based IrO2+Ta2O5 coating anodes
    Li Baosong
    Lin An
    Gan Fuxing
    RARE METALS, 2006, 25 : 645 - 649
  • [5] Study on electrocatalytic properties of TiN based IrO2+Ta2O5 coating anodes
    Jiang Junfeng
    Xu Haibo
    Wang Tingyong
    Wang Jia
    Xu Likun
    Cheng Guang
    RARE METAL MATERIALS AND ENGINEERING, 2007, 36 (02) : 344 - 348
  • [6] Study on electrocatalytic properties of TiN based IrO2+Ta2O5 coating anodes
    Jiang, Junfeng
    Xu, Haibo
    Wang, Tingyong
    Wang, Jia
    Xu, Likun
    Cheng, Guang
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2007, 36 (02): : 344 - 348
  • [7] Effect of preparation conditions on the properties of Ti based IrO2+Ta2O5 anodes
    Jinshu Xuebao/Acta Metallurgica Sinica, 2002, 38 (01):
  • [8] Effect of preparation conditions on the properties of Ti based IrO2+Ta2O5 anodes
    Hu, JM
    Meng, HM
    Zhang, JQ
    Cao, CN
    ACTA METALLURGICA SINICA, 2002, 38 (01) : 69 - 73
  • [9] Preparation of titanium based IrO2+Ta2O5 gradient coating anodes and their electrocatalytic properties
    Pang H.-L.
    Meng P.-J.
    Zhang Y.-P.
    Yang Y.
    Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2018, 28 (02): : 327 - 333
  • [10] Aging performances of Ti based IrO2+Ta2O5 anodes in sulfuric acid during electrolysis
    Hu, JM
    Meng, HM
    Zhang, JQ
    Cao, CN
    ACTA PHYSICO-CHIMICA SINICA, 2002, 18 (01) : 14 - 20