Alkali Metal Ion Insertion in Polypyrrole Polyoxometalates for Multifunctional Actuator-Sensor-Energy Storage Devices

Modern research technology's goal is to produce multifunctional materials that require low energy. In this work, we have applied polypyrrole (PPy) doped with dodecyl benzenesulfonate (DBS-) with the addition of polyoxometalates (POM) such as phosphotungstic acid (PTA) forming PPyDBS-PT composites. Two different PTA concentrations (4 mM and 8 mM) were used to form PPyDBS-PT4 and PPyDBS-PT8. The higher concentration of PTA created a highly dense and compact film which can be observed from scanning electron microscopy (SEM cross-section image), and also contains fewer phosphotungstate anions (PT3-) inclusion (via energy-dispersive X-ray spectroscopy, EDX). Three different aqueous electrolytes, LiCl (lithium chloride), NaCl (sodium chloride), and KCl (potassium chloride), were applied to investigate how those alkali metal ions perform as typical cation-driven actuators. Cyclic voltammetry with linear actuation revealed the tendency LiCl > NaCl > KCl in view of better strain, charge density, electronic conductivity, and Young's modulus of PPyDBS-PT4 outperformed PPyDBS-PT8. Chronopotentiometric measurements showed high specific capacitance for PPyDBS-PT4 at 260.6 +/- 21 F g(-1) with capacity retention after 5000 cycles of 88.5%. The sensor calibration of PPyDBS-PT4 revealed that the alkali cations (Li+, Na+, and K+) can be differentiated from each other. The PPyDBS-PT4 has multifunctional applications such as actuators, sensors, and energy storage.