Design and Heat Transfer Analysis of Graphene-Based Electric Heating Solid Wood Composite Energy Storage Flooring

Due to severe global energy issues and the widespread demand for high-quality winter heating, this study designed a new type of graphene-based electrically heated solid wood composite floor. This flooring maintains the convenience of a traditional floor installation while providing users with a more comfortable living experience. Additionally, the low-temperature heating and temperature regulation system further reduces energy consumption, offering a new perspective for green home living. This paper introduces the overall structure and temperature control system of the graphene-heated solid wood composite flooring. Based on the above reasons, the working mechanism and heat transfer process of the graphene-heated flooring were analyzed, and a mathematical model was established. Furthermore, simulations of flooring with different thicknesses were conducted to determine temperature rise curves and corresponding times. Finally, a comparative experimental verification was conducted on the thermodynamic performance of the solid wood composite graphene flooring. The results showed that in the case of a floor with an 18 mm thickness, the time for the surface layer of the floor to reach 22 degrees C is 27 min; the time to reach 26 degrees C is 56 min; and that the time to reach 28 degrees C is 109 min. The time required to return to 22 degrees C after the power has been switched off is 25 min. The results also showed that one hour after the power was turned off, the surface temperature of the floor was still above 20 degrees C. The study shows that the graphene-heated flooring can be used to achieve high-quality heating.