Corrosion behavior of anodized 6061 aluminum alloy in industrial-marine atmosphere in Qingdao after long-term exposure

被引：0
|
作者：
Zhao Q.-Y. [1 ]
Jia Z.-H. [1 ]
Zhao J.-B. [2 ,3 ]
Huang Y.-H. [1 ]
Cheng X.-Q. [1 ]
Li X.-G. [1 ]
机构：
[1] Institution of Advanced Materials and Technology, University of Science and Technology Beijing, Beijing
[2] Nanjing Iron and Steel Co., Ltd., Nanjing
[3] Jiangsu Key Laboratory for Premium Steel Material, Nanjing
来源：
Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals | 2020年 / 30卷 / 06期
基金：
中国国家自然科学基金;
关键词：
Anodized 6061 aluminum alloy; Industrial-marine atmospheric environment; Intergranular corrosion; Mechanical properties; Pitting corrosion;
D O I：
10.11817/j.ysxb.1004.0609.2020-36426
中图分类号：
学科分类号：
摘要：
The outdoor exposure tests of anodized 6061 aluminum alloy in sulfuric acid and boron-sulfuric acid were carried in industrial-marine atmospheric environment at Qingdao for five years. The effects of two different anodizing methods on the corrosion behavior and mechanism of 6061 aluminum alloy were investigated by means of the surface and cross-section morphology observation, mass loss method, the corrosion products analysis, mechanical properties testing and fracture analysis. The results show that the average corrosion rates of the anodized alloy in sulfuric acid and boron-sulfuric acid decrease by 70.2% and 45.4% after five-year exposure in the industry-marine atmospheric environments, respectively, compared to the naked alloy. The loss of yield strength decrease by 69.5% and 11.0%, and the loss of elongation decrease by 71.8% and 41.0%. Thus, the anodic treatment weakened corrosion and the effect of sulfuric acid anodizing is much better than for the boron-sulfuric acid anodizing. The high concentration of chloride ions in the industry-marine atmosphere in Qingdao plays an important role in the destruction of the oxide films and in inducing the pitting corrosion. Due to the pitting on the grain boundaries, the intergranular corrosion initiated. The sulfide in the atmosphere can penetrate into the grain boundary region along with the corrosive medium, which aggravate the propagation of the intergranular corrosion. The anodized film has an effective hindrance for chloride ions penetrating to the matrix, and the effect of anodizing in sulfuric acid is better, which can effectively inhibit the initiation and propagation of intergranular corrosion, thereby reduce the loss of strength and plasticity of 6061 aluminum alloys. © 2020, Science Press. All right reserved.
引用
收藏
页码：1249 / 1262
页数：13
相关论文
共 26 条
  • [1] ABDEL-GAWAD S A, OSMAN W M, FERKRY A M., Characterization and corrosion behavior of anodized aluminum alloys for military industries applications in artificial seawater, Surfaces and Interfaces, 14, pp. 314-323, (2019)
  • [2] MOKHTARI S, KARIMZADEH F, ABBASI M H, RAEISSI K., Development of super-hydrophobic surface on Al 6061 by anodizing and the evaluation of its corrosion behavior, Surface and Coatings Technology, 324, 14, pp. 99-105, (2017)
  • [3] SUN Fei-long, LI Xiao-gang, LU Lin, CHENG Xue-qun, DONG Chao-fang, GAO Jin, Corrosion behavior of 5052 and 6061 aluminum alloys in deep ocean environment of south china sea, Acta Metallurgica Sinica, 49, 10, pp. 1219-1226, (2013)
  • [4] ZHANG Xin-ming, DENG Yun-lai, ZHANG Yong, Development of high strength aluminum alloys and processing techniques for the materials J], Acta Metallurgica Sinica, 51, 3, pp. 257-271, (2015)
  • [5] VARMA S K, ANDREWS S, VASQUEZ G., Corrosive wear behavior of 2014 and 6061 aluminum alloy composites, Journal of Materials Engineering and Performance, 8, 1, pp. 98-102, (1999)
  • [6] GONG Peng, ZHENG Lin-bin, YI Lin-na, SONG De-yu, Effects of hole cold-expansion on microstructure and fatigue property of 7B50-T7451 aluminum alloy plate, Journal of Aeronautical Materials, 31, 4, pp. 45-50, (2011)
  • [7] HUANG Yan-bin, ZHONG Liu-shi, SONG Gao-wei, LI Xiao-ming, Application of anodic oxidation in surface bonding technology of aluminum, Equipment Environmental Engineering, 9, 3, pp. 71-74, (2012)
  • [8] LUO Yi-fan, XU Xuan, CHEN Xue-wen, ZHOU Ai-qun, LUO Li-qing, Aluminum alloy anodizing process with sulfuric acid as major salt, Electroplating & Finishing, 1, pp. 33-35, (2004)
  • [9] CRITCHLOW G W, YENDALL K A, BAHRANI D, QUINN A, ANDREWS F., Strategies for the re-placement of chromic acid anodising for the structural bonding of aluminum alloys, International Journal of Adhesion & Adhesives, 26, 6, pp. 419-453, (2006)
  • [10] WANG Shuai-xing, ZHAO Qing, DU Nan, SHAO Zhi-song, SHU Wei-fa, CHEN Qing-long, Sealing effect of cerium salt on boric-sulfuric acid anodic film of aluminum alloy, The Chinese Journal of Nonferrous Metals, 22, 4, pp. 1132-1141, (2012)
123