Research on Formation Mechanisms of Gradient Structures for WC-TiC-Co Carbides Under Vacuum and Nitriding Sintering

被引：0

作者：

Chen J. ^{[1
,2
]}

Zhou L. ^{[1
]}

Liu J. ^{[2
]}

Ji H. ^{[2
]}

Yang Y. ^{[1
]}

Liu W. ^{[2
]}

Deng X. ^{[2
]}

Wu S. ^{[2
]}

机构：

[1] School of Mechatronic Engineering, Guangdong Polytechnic Normal University, Guangzhou

[2] School of Electromechanical Engineering, Guangdong University of Technology, Guangzhou

来源：

Cailiao Daobao/Materials Reports | 2020年 / 34卷 / 02期

基金：

广东省科技计划;

关键词：

Cemented carbide; Gradient structure; Microstructure; Sintering atmosphere;

D O I：

10.11896/cldb.18110198

中图分类号：

学科分类号：

摘要：

This paper has systematically investigated the gradient microstructures in WC-20TiC-0.5VC-0.5Cr2C3-12Co cemented carbides synthesized in vacuum and nitriding sintering, respectively. The study shows that sintering atmosphere has a critical effect on gradient structure of WC-TiC-Co carbide. The vacuum sintering results in a surface layer free of face center cubic (FCC) phase. The thickness of FCC-free surface layer is more than 20 μm. The nitriding sintering results in the formation of a FCC (Ti(C,N) and TiC) rich surface layer. It shows that N2 pressure has an important effect on the thickness of FCC-rich surface layer. The higher N2 pressure results in the thicker FCC-rich surface layer. The microstructure in the core of the carbides synthesized in either vacuum or nitriding sintering atmosphere shares similar microstructure of WC, (W,Ti)C, TiC and Co phases. Compared with nitriding sintering, vacuum sintering leads to coarser WC grains in the core of the carbide. © 2020, Materials Review Magazine. All right reserved.

引用

页码：04077 / 04082

页数：5

共 21 条

[1] Upadhyaya G., Materials and Design, 22, 6, (2001)
[2] Van-Der-Merwe R., Sacks N., International Journal of Refractory Metals and Hard Materials, 41, (2013)
[3] Wang Y., Pan Z., Wang C., Et al., Journal of Materials Science & Technology, 28, 3, (2012)
[4] Espinosa L., Bonache V., Salvador M.D., Wear, 272, 1, (2011)
[5] Yang Y., Su Y., Li L., Et al., The International Journal of Advanced Manufacturing Technology, 76, 9-12, (2014)
[6] Hei H., Ma J., Li X., Et al., Surface and Coatings Technology, 261, (2015)
[7] Konyashin I., Ries B., Hlawatschek S., Surface and Coatings Technology, 258, (2014)
[8] Liu Y., Li X., Zhou J., Et al., International Journal of Refractory Metals and Hard Materials, 50, (2015)
[9] Shi L., Yang J., Huang J., Et al., International Journal of Refractory Metals & Hard Materials, 66, (2017)
[10] Suzuki H., Hayashi K., Taniguchi Y., Transactions of the Japan Institute of Metals, 22, 11, (2007)

← 1 2 3 →