Corrosion Properties of Cold-Sprayed Cr3C2-25(Ni20Cr) Coatings After Heat Treatment

The corrosion resistance of a Cr3C2-25(Ni20Cr) cermet coating applied to an Al7075 substrate (Cr3C2-25(Ni20Cr)/Al7075) was investigated. The coating was produced using a cold spraying (CS) method. The main aim of the research was to determine the effect of heat treatment on the properties of cermet coatings on the Al7075 substrate. The mechanical properties of the Cr3C2-25(Ni20Cr)/Al7075 composite were assessed through microhardness (HV) measurements. The surface morphology and microstructure of the specimens were examined using a scanning electron microscope (SEM). Electrochemical testing in an acidic chloride solution was employed to evaluate the corrosion behavior of the materials. The cermet coating effectively protected the Al7075 substrate from the aggressive corrosive environment. Heat treatment homogenized the structure of the cermet coating, eliminating microcracks and pores on the Cr3C2-25(Ni20Cr)/Al7075 surface. Notably, annealing at 300 degrees C in air significantly enhanced the corrosion resistance of the cermet coating. The corrosion rate was reduced by more than five times compared to the non-heat-treated Cr3C2-25(Ni20Cr)/Al7075 coating.