Effects of sulfur oxyanions and magnetite on the corrosion behavior of alloy 600 under simulated PWR secondary water conditions

被引：0
|
作者：
Han, Jeoh [1 ,2 ]
Hur, Do Haeng [1 ]
Song, Geun Dong [3 ]
Jeon, Soon-Hyeok [1 ]
机构：
[1] Korea Atom Energy Res Inst, Mat Safety Technol Res Div, Daejeon, South Korea
[2] Korea Hydro & Nucl Power Co Ltd, Cent Res Inst, Daejeon, South Korea
[3] FNC Technol Co Ltd, Nucl Mat Res Grp, Gyeonggi Do, South Korea
来源：
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T | 2024年 / 33卷
基金：
新加坡国家研究基金会;
关键词：
Alloy; 600; Sulfur oxyanions; Magnetite; Corrosion; Oxide film; Potentiodynamic polarization; GENERATOR TUBING ALLOYS; GALVANIC CORROSION; QUANTITATIVE ASSESSMENT; CHLORIDE-IONS; CRACKING; STRESS; LEAD; TEMPERATURE; THIOSULFATE; SULFATE;
D O I：
10.1016/j.jmrt.2024.11.270
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
This study investigates the corrosion behavior of Alloy 600 in sulfur oxyanions (sulfate and tetrathionate) solutions. The corrosion rate and oxide thickness of Alloy 600 drastically increase by the presence of sulfur oxyanions in the environment. The phenomenon is mainly caused by tetrathionate ions, not sulfate ions. When Alloy 600 and magnetite are electrically connected in the solutions, they respectively behave as an anode and a cathode. This galvanic coupling effect further accelerates the corrosion of Alloy 600. The preferential dissolution of Ni and reduction of tetrathionate result in the formation of an oxide layer composed of Ni-depleted Cr-Fe oxides and Ni3S2 compounds.
引用
收藏
页码：9693 / 9702
页数：10
相关论文
共 50 条
  • [1] Combined effects of lead and magnetite on the stress corrosion cracking of alloy 600 in simulated PWR secondary water
    Song, Geun Dong
    Choi, Won-Ik
    Jeon, Soon-Hyeok
    Kim, Jung Gu
    Hur, Do Haeng
    JOURNAL OF NUCLEAR MATERIALS, 2018, 512 : 8 - 14
  • [2] Magnetite Deposition Behavior on Alloy 600 and Alloy 690 Tubes in Simulated PWR Secondary Water
    Jeon, Soon-Hyeok
    Lee, Yong-Beom
    Lee, Kyung-Hee
    Hur, Do-Haeng
    COATINGS, 2022, 12 (09)
  • [3] Corrosion Behavior of Alloy 600 Coupled with Electrodeposited Magnetite in Simulated Secondary Water of PWRs
    Jeon, Soon-Hyeok
    Song, Geun-Dong
    Hur, Do Haeng
    MATERIALS TRANSACTIONS, 2015, 56 (12) : 2078 - 2083
  • [4] Effects of reduced sulfur on the corrosion behavior of Alloy 600 in high-temperature water
    Lee, E. H.
    Kim, K. M.
    Kim, U. C.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 449 : 330 - 333
  • [5] Stress Corrosion Cracking Behavior of Alloy 600 Coupled to Magnetite under High-Temperature Caustic Conditions
    Song, Geun Dong
    Han, Jeoh
    Jeon, Soon-Hyeok
    Hur, Do Haeng
    MATERIALS, 2019, 12 (13)
  • [6] Semiconducting behavior and bandgap energies of oxide films grown on alloy 600 under PWR simulated primary water conditions with different dissolved hydrogen contents
    Loucif, A.
    Petit, J-P
    Wouters, Y.
    JOURNAL OF NUCLEAR MATERIALS, 2013, 443 (1-3) : 222 - 229
  • [7] Stress corrosion crack growth rates of alloy 600 in simulated PWR coolant
    Magdowski, R
    Vaillant, F
    Amzallag, C
    Speidel, O
    PROCEEDINGS OF THE EIGHTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS - WATER REACTORS, VOLS 1 AND 2, 1997, : 333 - 339
  • [8] Study on electrochemical behavior of 690 alloy with corrosion products in simulated PWR primary water environment
    Cheng, Xuequn
    Zuo, Xiao Mei
    ANTI-CORROSION METHODS AND MATERIALS, 2018, 65 (06) : 616 - 625
  • [9] Stress corrosion crack initiation of alloy 600 in PWR primary water
    Zhai, Ziqing
    Toloczko, Mychailo B.
    Olszta, Matthew J.
    Bruemmer, Stephen M.
    CORROSION SCIENCE, 2017, 123 : 76 - 87
  • [10] EFFECTS OF VARIATIONS OF CARBON, SULFUR AND PHOSPHORUS ON CORROSION BEHAVIOR OF ALLOY-600
    MCILREE, AR
    MICHELS, HT
    MORRIS, PE
    CORROSION, 1975, 31 (12) : 441 - 448
12345