The Influence of the Steam Sterilization Process on Selected Properties of Polymer Samples Produced in MEX and JMT Processes

Polymeric materials are widely used in medical engineering, and with the dynamic development of additive manufacturing (AM) technology, increasing attention is being paid to research on the mechanical strength of composite polymer structures. At the same time, the impact of sterilization on, for example, surgical templates and the influence of the sterilization process on the geometry of these parts have not been sufficiently studied. In this work, the effect of steam sterilization on samples made of polymer materials for medical applications was presented. This research was carried out on samples with normative geometry made of polyetheretherketone (PEEK) polymers produced using the Material Extrusion (MEX) AM process and acrylic formulation (MED610) produced by Jetting Modeling Technology (JMT). These materials provide biocompatibility, which makes them suitable for potential medical applications. Steam sterilization was performed in an autoclave at temperatures of 121 degrees C and 134 degrees C. The three-point bending strength properties were determined according to ISO 178 standards. An INSTRON 5967 strength testing machine was used for those tests. Surface roughness analysis (according to ISO 21920) was performed and presented in 2D and 3D surface views using the Mountains Map Software (version 6.0).