Low-Cycle Fatigue of a Nickel Superalloy at Various Loading Frequencies

被引：0
|
作者：
Ryzhkov, P. V. [1 ]
Gorbovets, M. A. [1 ]
Khodinev, I. A. [1 ]
机构：
[1] VIAM, Natl Res Ctr Kurchatov Inst, Moscow 105005, Russia
来源：
RUSSIAN METALLURGY | 2024年 / 2024卷 / 02期
关键词：
low cycle fatigue; strain-controlled loading; total deformation amplitude; loading frequency; nickel superalloy; ELEVATED-TEMPERATURE; STRAIN-RATE; BEHAVIOR; TENSILE; DWELL; TIME;
D O I：
10.1134/S003602952470085X
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The influence of the deformation frequency in a low-cycle region (f = 1-3 Hz, N <= 10(5) cycles) on the fatigue life characteristics of a nickel superalloy has been studied. Tests are performed under strain-controlled loading conditions at temperatures of 25 and 700 degrees C. The influence of the deformation frequency on the fatigue life is found to be most significant at an elevated temperature. The main difference in the character of fracture consists in a flatter fracture surface relief and a longer fatigue crack front at an increased loading frequency.
引用
收藏
页码：495 / 500
页数：6
相关论文
共 50 条
  • [1] Low-Cycle Fatigue of a VZh175 Nickel Superalloy during Asymmetric Loading
    M. A. Gorbovets
    I. A. Khodinev
    M. S. Belyaev
    P. V. Ryzhkov
    Russian Metallurgy (Metally), 2019, 2019 : 889 - 893
  • [2] Low-Cycle Fatigue of a VZh175 Nickel Superalloy during Asymmetric Loading
    Gorbovets, M. A.
    Khodinev, I. A.
    Belyaev, M. S.
    Ryzhkov, P. V.
    RUSSIAN METALLURGY, 2019, 2019 (09): : 889 - 893
  • [3] Low-Cycle Fatigue of Nickel Superalloy Single Crystals at Elevated Temperatures
    Golubovskiy, E. R.
    Svetlov, I. L.
    Petrushin, N. V.
    Cherkasova, S. A.
    Volkov, M. E.
    RUSSIAN METALLURGY, 2010, 2010 (10): : 941 - 947
  • [4] MEAN STRESS MODELS FOR LOW-CYCLE FATIGUE OF A NICKEL-BASE SUPERALLOY
    FANG, DN
    BERKOVITS, A
    INTERNATIONAL JOURNAL OF FATIGUE, 1994, 16 (06) : 429 - 437
  • [5] METHOD OF LOW-CYCLE FATIGUE TESTS WITH NONPROPORTIONAL LOW-CYCLE LOADING
    KAZANTSEV, AG
    INDUSTRIAL LABORATORY, 1986, 52 (12): : 1139 - 1141
  • [6] MICROSTRUCTURAL EFFECTS ON THE LOW-CYCLE FATIGUE BEHAVIOR OF A HIPD NICKEL-BASE SUPERALLOY
    CROMPTON, JS
    VECCHIO, RS
    HERTZBERG, RW
    JOURNAL OF METALS, 1984, 36 (12): : 83 - 83
  • [7] DISCUSSIONS - LOW-CYCLE FATIGUE CHARACTERISTICS OF A NICKEL-BASE SUPERALLOY AT ROOM TEMPERATURE
    MANSON, SS
    SPERA, DA
    WELLS, CH
    ASM TRANSACTIONS QUARTERLY, 1965, 58 (04): : 749 - &
  • [8] Low-Cycle Fatigue Behavior of a Nickel Base Single Crystal Superalloy at High Temperature
    Shui Li
    Liu Ping
    RARE METAL MATERIALS AND ENGINEERING, 2015, 44 (02) : 288 - 292
  • [9] Cyclic softening of an under-aged nickel base superalloy in low-cycle fatigue
    Ferney, W
    COMPTES RENDUS DE L ACADEMIE DES SCIENCES SERIE II FASCICULE B-MECANIQUE, 2001, 329 (12): : 843 - 850
  • [10] Rapid extrapolation of high-temperature low-cycle fatigue curves for a nickel superalloy
    Viespoli L.M.
    Berto F.
    Material Design and Processing Communications, 2019, 1 (06):
12345