On the utilization of high rate pre-cracked Charpy test results and the master curve to obtain accurate lower bound toughness predictions in the ductile-to-brittle transition

被引：0

|

作者：

Joyce, James A. ^{[1
]}

机构：

[1] Department of Mechanical Engineering, U.S. Naval Academy, Annapolis, MD 21402, United States

来源：

ASTM Special Technical Publication | 1998年 / 1329期

关键词：

D O I：

暂无

中图分类号：

学科分类号：

摘要：

引用

收藏

页码：253 / 273

相关论文

共 5 条

[1] On the utilization of high rate pre-cracked Charpy test results and the master curve to obtain accurate lower bound toughness predictions in the ductile-to-brittle transition
Joyce, JA
SMALL SPECIMEN TEST TECHNIQUES, 1998, 1329 : 253 - 273
[2] Fracture toughness characterisation in the ductile-to-brittle transition and upper shelf regimes using pre-cracked Charpy single-edge bend specimens
Heerens, J
Ainsworth, RA
Moskovic, R
Wallin, K
INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2005, 82 (08) : 649 - 667
[3] BRITTLE-DUCTILE TRANSITION CURVE DETERMINED BY CHARPY IMPACT TESTING ON CVN, PRE-CRACKED CVN AND SIDE-GROOVED PRE-CRACKED CVN SPECIMENS
NGUYENDUY, P
BAYARD, S
INTERNATIONAL JOURNAL OF FRACTURE, 1982, 18 (02) : R23 - R29
[4] ON THE USE OF THE NOTCH MASTER CURVE FOR APPARENT FRACTURE TOUGHNESS PREDICTIONS OF NOTCHED FERRITIC STEELS OPERATING WITHIN THE DUCTILE-TO-BRITTLE TRANSITION ZONE
Cicero, Sergio
Garcia, Tiberio
Madrazo, Virginia
ASME PRESSURE VESSELS AND PIPING CONFERENCE - 2015, VOL 6B, 2015,
[5] Experimental investigation of scatter in fracture toughness data of SA516Gr.70 steel in the ductile-to-brittle transition regime for high rate of loading using split Hopkinson pressure bar test setup
Sharma, S.
Samal, M. K.
ENGINEERING FAILURE ANALYSIS, 2021, 122