Influence of Cold Deformation on the Fracture Behavior of Welds.

被引：0
|
作者：
Povse, Th.
Wallner, F.
Ornig, H.
机构：
来源：
Berg- und Huettenmaennische Monatshefte | 1973年 / 118卷 / 03期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Title investigation was carried out by a committee composed of representatives of leading, Austrian, Metallurgical research organizations that was using the notch-impact-bending-, and Pellim tests. Influence of the straightening of welds was noticeable by the increse of transition temperature of the welds. Assessment of the fracture behavior of the three, investigated welding materials led to widely differing values, pointing out the need for further, intensive research.
引用
收藏
页码：66 / 72
相关论文
共 50 条
  • [1] FRACTURE TOUGHNESS OF STEEL-ALUMINUM DEFORMATION WELDS.
    Albright, C.E.
    Welding Journal (Miami, Fla), 1981, 60 (11):
  • [2] Deformation Curves for Fillet Welds.
    Anon
    Soudage et Techniques Connexes, 1982, 36 (9-10): : 375 - 379
  • [3] FRACTURE TOUGHNESS TESTING OF WELDS.
    Soete, W.
    Denys, R.
    Revue de la Soudure/Lastijdschrift, 1977, 33 (01): : 7 - 14
  • [4] Investigation of the Factors Causing Fracture in Polyethylene Pipeline Welds.
    Sajzew, K.I.
    ZIS Mitteilungen, 1977, 19 (03): : 338 - 347
  • [5] INFLUENCE OF WELD MISALIGNMENT AND WELD METAL OVERMATCH ON THE PREDICTION OF FRACTURE IN PIPELINE GIRTH WELDS.
    Worswick, M.J.
    Pick, R.J.
    1600, (21):
  • [6] Failure of Welds.
    Kurz, Richard
    Schweissen und Schneiden/Welding and Cutting, 1973, 25 (02): : 48 - 52
  • [7] Application of heuristic fracture mechanics methods to the safety evaluation of welds.
    Bartholome, G
    Senski, G
    PROCEEDINGS OF THE INTERNATIONAL CONFERENCE ON WELDED STRUCTURES IN PARTICULAR WELDED BRIDGES, 1996, : 221 - 231
  • [8] Hydrogen-Induced Cold Cracking: Cracks Adjacent to Welds.
    Moeser, Martin
    Schweisstechnik Berlin, 1985, 35 (03): : 140 - 143
  • [9] Fracture Mechanics Analysis of Crack Propagation in Rails and Rail Welds.
    Edel, Karl-Otto
    Schweisstechnik Berlin, 1985, 35 (12): : 555 - 558
  • [10] EFFECT OF MECHANICAL HETEROGENEITY ON FRACTURE TOUGHNESS EVALUATION OF STEEL WELDS.
    Satoh, Kunihiko
    Toyoda, Masao
    Minami, Fumiyoshi
    Nakanishi, Mutsuo
    Arimochi, Kazushige
    Satoh, Susumu
    Transactions of the Japan Welding Society, 1985, 16 (02): : 170 - 177
12345