PREVENTING DELAYED CRACKS IN SHIP WELDS.

被引：0

作者：

Mishler, H.W.

机构：

来源：

Ship Structure Committee (Report) SSC (United States) | 1976年

关键词：

SHIPBUILDING - Welding - WELDING - Personnel Training;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Delayed cracking is a continuing problem in ship steel weldments. However, with proper precautions, this type of cracking can be prevented. This document presents, in a simplified and condensed form, the causes of delayed cracking and the necessary preventive procedures. It is intended that this document will be used by shipyard personnel that do not have a technical background. Thus, detailed technical explanations are avoided.

引用

共 50 条

[1] Effect of Cracks on the Load Capacity of Welds.
Gliha, Vladimir
1600, (30): : 11 - 12
[2] TRACKING DOWN CRACKS IN BOILER TUBE WELDS.
Bangs, Scholer
Welding Design and Fabrication, 1979, 52 (10): : 74 - 79
[3] EFFECT OF PLATE THICKNESS ON CRACKS OF UNDERWATER WELDS.
Hasegawa, Masayoshi
Chubu Daigaku Kogakubu Kiyo/Memoirs of College of Engineering Chubu University, 1986, 22 : 1 - 7
[4] Welding Cracks in EI-835 Steel Welds.
Mikula, Jozef
Przeglad Mechaniczny, 1986, 45 (24): : 9 - 13
[5] Hydrogen-Induced Cold Cracking: Cracks Adjacent to Welds.
Moeser, Martin
Schweisstechnik Berlin, 1985, 35 (03): : 140 - 143
[6] Failure of Welds.
Kurz, Richard
Schweissen und Schneiden/Welding and Cutting, 1973, 25 (02): : 48 - 52
[7] Reinforcing fillet welds preventing cracks in partial joint penetration welds
Badrkhani Ajaei, B.
Ghassemieh, M.
INTERNATIONAL JOURNAL OF STEEL STRUCTURES, 2015, 15 (02) : 487 - 497
[8] Reinforcing fillet welds preventing cracks in partial joint penetration welds
B. Badrkhani Ajaei
M. Ghassemieh
International Journal of Steel Structures, 2015, 15 : 487 - 497
[9] ULTRASONIC INSPECTION OF CORROSION-FATIGUE CRACKS IN AUSTENITIC STAINLESS STEEL WELDS.
Kapranos, P.A.
Whittaker, V.N.
British Journal of Non-Destructive Testing, 1984, 26 (01): : 15 - 19
[10] Loading of Plug Welds.
Moebius, W.
Seyffarth, W.
Mueller, H.
Schweisstechnik Berlin, 1983, 33 (09): : 401 - 404

← 1 2 3 4 5 →