Corrosion-fatigue behaviour of Ti-75 titanium alloy

被引：0
|
作者：
Meng, Liang [1 ]
Huan, Hong [1 ]
Li, Zuochen [1 ]
机构：
[1] Northwest Inst for Nonferrous Metal, Research, Baoji, China
来源：
Xiyou jinshu cailiao yu gongcheng | 1994年 / 23卷 / 03期
关键词：
Corrosion fatigue - Fatigue testing - Metallographic microstructure;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
An self-designed automatic liquor cycling unit for fatigue testing was introduced, and the experimental research of corrosion-fatigue properties of Ti-75 titanium alloy was carried out. The fatigue limits of 1×107 cycles determined in air and in 3.5wt% NaCl aqueous solution at room temperature are 392 MP and 431 MPa respectively. The results indicate that the corrosion-fatigue properties of Ti-75 alloy increase by a factor of 29% in air and 26% in 3.5wt% NaCl aqueous solution, as compared with TA5 alloy. The improvements of the properties shown above are related to the microstructure of Ti-75 alloy.
引用
收藏
页码：40 / 44
相关论文
共 50 条
  • [1] CORROSION-FATIGUE OF TI 29 ALLOY IN A SOUR BRINE ENVIRONMENT
    Hudak, Stephen J., Jr.
    Robledo, Guadalupe B.
    Feiger, James H.
    33RD INTERNATIONAL CONFERENCE ON OCEAN, OFFSHORE AND ARCTIC ENGINEERING, 2014, VOL 5, 2014,
  • [2] Investigation of the Processes of Fatigue and Corrosion-Fatigue Destruction of Pseudo-α Titanium Alloy
    Murashov, A. A.
    Berendeyev, N. N.
    Nokhrin, A., V
    Galaeva, E. A.
    Chuvil'deev, V. N.
    INORGANIC MATERIALS-APPLIED RESEARCH, 2022, 13 (02) : 349 - 356
  • [3] Investigation of the Processes of Fatigue and Corrosion-Fatigue Destruction of Pseudo-α Titanium Alloy
    A. A. Murashov
    N. N. Berendeyev
    A. V. Nokhrin
    E. A. Galaeva
    V. N. Chuvil’deev
    Inorganic Materials: Applied Research, 2022, 13 : 349 - 356
  • [4] Casting behavior of the dental alloy Ti-75
    Zhang, YM
    Guo, TW
    Li, ZC
    Li, CL
    RARE METAL MATERIALS AND ENGINEERING, 1999, 28 (02) : 125 - 128
  • [5] Corrosion-fatigue crack growth in titanium alloys
    Gregory, JK
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 1999, 50 (01): : 7 - 11
  • [6] A peridynamic model for corrosion-fatigue failure behaviour
    Wu, Haoqi
    Qi, Hongyu
    Li, Shaolin
    Zhao, Gaole
    Yang, Xiaoguang
    Shi, Duoqi
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2023, 127
  • [7] Influence of incomplete annealing of titanium (a + β)-alloy and its welded joints on fatigue resistance and corrosion-fatigue resistance
    O. S. Kalakhan
    V. I. Pokhmurs’kyi
    Materials Science, 2000, 36 : 244 - 251
  • [8] CORROSION-FATIGUE RESISTANCES OF SURGICAL IMPLANT STAINLESS-STEELS AND TITANIUM-ALLOY
    YU, J
    ZHAO, ZJ
    LI, LX
    CORROSION SCIENCE, 1993, 35 (1-4) : 587 - 597
  • [9] Corrosion-Fatigue Effect on the Life of Aluminum Alloy
    Wang, Fusheng
    Zhang, Xuntao
    Wang, Ailun
    Chen, Yajun
    MATERIALS PERFORMANCE, 2018, 57 (08) : 54 - 57
  • [10] Corrosion-fatigue effect on the life of aluminum alloy
    2018, NACE International (57)
12345