Relation between crossover of the intergrain loss-peak temperature-field characteristics of the Ag-Bi2Sr2CaCu2Ox screen-printed tapes and their Jc values

被引：0
|
作者：
机构：
[1] Noji, H.
[2] Glowacki, B.A.
[3] Oota, A.
来源：
Noji, H. | 1600年 / 195期
关键词：
Bismuth compounds - Calcium compounds - Copper compounds - Copper oxides - High temperature superconductors - Oxides - Silver - Strontium compounds - Substrates - Tapes;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A study of the influence of the processing conditions of Ag-Bi2Sr2CaCu2Ox screen-printed tapes on the temperature, field and frequency dependence of their a.c. susceptibility has been conducted. Samples have been prepared by melt-solidification and subsequent sintering on silver substrates under the same conditions but with different cooling procedures and reannealing. These procedures lead to different Tc values and field dependency of the loss peak temperature TM, which cause the crossover in the TM versus applied field characteristics. It was established that the above crossover phenomenon is correlated to the crossover in the Jc versus temperature characteristics.
引用
收藏
页码：1 / 2
相关论文
共 25 条
  • [1] THE RELATION BETWEEN CROSSOVER OF THE INTERGRAIN LOSS-PEAK TEMPERATURE-FIELD CHARACTERISTICS OF THE AG-BI2SR2CACU2OX SCREEN-PRINTED TAPES AND THEIR JC VALUES
    NOJI, H
    GLOWACKI, BA
    OOTA, A
    JOURNAL OF ALLOYS AND COMPOUNDS, 1993, 195 (1-2) : 639 - 642
  • [2] INFLUENCE OF COOLING AND ANNEALING PROCEDURE ON THE INTERGRANULAR COUPLING OF AG-BI2SR2CACU2OX SCREEN-PRINTED TAPE
    NOJI, H
    ZHOU, W
    GLOWACKI, BA
    OOTA, A
    PHYSICA C, 1993, 205 (3-4): : 397 - 405
  • [3] IMPROVEMENTS OF MICROSTRUCTURAL AND SUPERCONDUCTING PROPERTIES OF AG-BI2SR2CACU2OX SCREEN-PRINTED TAPE BY CONTROLLED OXYGEN PARTIAL-PRESSURE DURING COOLING PROCEDURE
    NOJI, H
    ZHOU, W
    GLOWACKI, BA
    OOTA, A
    APPLIED PHYSICS LETTERS, 1993, 63 (06) : 833 - 835
  • [4] Local Jc distribution in superconducting oxide layer of Bi2Sr2CaCu2Ox/Ag tapes
    Hishinuma, Y
    Kitaguchi, H
    Kumakura, H
    Itoh, K
    Togano, K
    Miao, HP
    Chenevier, B
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 1999, 9 (02) : 1908 - 1911
  • [5] Current-voltage characteristics of Bi2Sr2CaCu2Ox tapes with and without Ag sheath
    Polak, M
    Zhang, W
    Hellstrom, EE
    Larbalestier, DC
    APPLIED SUPERCONDUCTIVITY 1995, VOLS. 1 AND 2: VOL 1: PLENARY TALKS AND HIGH CURRENT APPLICATIONS; VOL 2: SMALL SCALE APPLICATIONS, 1995, 148 : 427 - 430
  • [6] CHARACTERISTICS OF STRENGTHENED AG SUBSTRATES FOR BI2SR2CACU2OX DOCTOR-BLADED TAPES
    NOMURA, K
    SATO, J
    KUMA, S
    KUMAKURA, H
    TOGANO, K
    TOMITA, N
    APPLIED PHYSICS LETTERS, 1994, 64 (07) : 912 - 914
  • [7] HIGH TRANSPORT CRITICAL CURRENTS IN FLEXIBLE SCREEN-PRINTED AG-(BI,PB)(2)SR2CA2CU3OX TAPES
    OOTA, A
    OGAWA, K
    MAEDA, J
    SHIBATA, K
    APPLIED PHYSICS LETTERS, 1995, 67 (06) : 854 - 856
  • [8] Magnetic field distributions in a remanent state of screen-printed Ag-(Bi,Pb)2Sr2Ca2Cu3Ox tapes with different superconductor geometries
    Oota, A
    Kawano, K
    Fujikawa, K
    Fujimoto, H
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1998, 11 (04): : 399 - 407
  • [9] Fabrication, microstructure and critical current density of screen-printed Ag-(Bi, Pb)2Sr2Ca2Cu3Ox superconducting tapes
    Oota, A., 1600, (210): : 3 - 4
  • [10] FABRICATION, MICROSTRUCTURE AND CRITICAL-CURRENT DENSITY OF SCREEN-PRINTED AG-(BI,PB)2SR2CA2CU3OX SUPERCONDUCTING TAPES
    OOTA, A
    MATSUI, H
    FUNAKURA, M
    IWAYA, J
    MITSUYAMA, K
    PHYSICA C, 1993, 210 (3-4): : 489 - 501
123