Studies of the Effect of the pH Value on the Corrosion of Brass.

被引：0
|
作者：
Resch, G.
Zinke, K.
机构：
来源：
VGB-Kraftwerkstechnik | 1980年 / 60卷 / 01期
关键词：
539 Metals Corrosion and Protection; Metal Plating - 544 Copper and Alloys - 546 Lead; Tin; Zinc; Antimony and Alloys;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The confirmation of all previous evidence of the corrosion-reducing effect of slightly increased pH values is considered an essential result of these experiments. This is valid both for ammonia as well as for caustic soda at 30 and 90 degree C in the presence of 1 to 2 mg/liter oxygen. As expected, in the presence of ammonia a corrosion minimum of between pH 8 and 9 was recorded.
引用
收藏
页码：62 / 64
相关论文
共 50 条
  • [1] INHIBITION OF ACID CORROSION OF BRASS.
    Pevneva, A.V.
    Gimasheva, I.M.
    Kamelin, V.V.
    Kuznetsov, V.V.
    1600, (21):
  • [2] The corrosion of brass. The structure of the corroded surface
    Stillwell, Charles W.
    Turnipseed, Edward S.
    PHYSICS-A JOURNAL OF GENERAL AND APPLIED PHYSICS, 1933, 4 (01): : 263 - 263
  • [3] The corrosion of a solid solution - 70/30 Brass.
    Gibbs, WE
    TRANSACTIONS OF THE FARADAY SOCIETY, 1916, 11 (2/3): : 0258 - 0266
  • [4] VERSATILE BRASS.
    Callcut, V.A.
    Metallurgist and materials technologist, 1984, 16 (09): : 471 - 474
  • [5] EFFECT OF ALLOYING ADDITIONS ON THE SUPERPLASTICITY OF BIPHASE BRASS.
    Portnoi, V.K.
    Levchenko, V.S.
    Kuin', Nguen Ngok
    Metal Science and Heat Treatment (English Translation of Metallovedenie i Termicheskaya Obrabotka, 1986, 28 (11-12): : 794 - 801
  • [6] Polyamide replaces brass.
    Hagen, R
    KUNSTSTOFFE-PLAST EUROPE, 1998, 88 (07): : 1030 - 1031
  • [7] A comparison screen for brass.
    Ellis, OW
    JOURNAL OF THE INSTITUTE OF METALS, 1917, 18 : 171 - 172
  • [8] Hot Stamping of Brass.
    Devroey, Pierre
    Metallurgie (Mons, Belgium), 1973, 13 (04): : 130 - 140
  • [9] The heat processing of brass.
    不详
    ZEITSCHRIFT DES VEREINES DEUTSCHER INGENIEURE, 1926, 70 : 1193 - 1193
  • [10] POWDER FORGING OF BRASS.
    Nakagawa, T.
    Amano, T.
    Hamai, T.
    Tanaka, T.
    Metal Powder Report, 1983, 38 (05) : 251 - 255
12345