ANODIC POLARIZATION OF Fe-Cr BINARY ALLOYS EMBRITTLED AT 475 degree C and Fe-Cr COUPLING ELECTRODE IN N-H2SO4 SOLUTION.

被引：0
|
作者：
Mito, Masaji
Sugawara, Hideo
机构：
来源：
Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals | 1974年 / 38卷 / 01期
关键词：
IRON AND ALLOYS - Anodic Oxidation - IRON AND STEEL METALLOGRAPHY - Etching;
D O I：
10.2320/jinstmet1952.38.1_22
中图分类号：
学科分类号：
摘要：
Potentiodynamic polarization experiment was performed on a number of Fe-Cr binary alloys in N-H//2SO//4 solution with prolonged 475 degree C embrittlement. The curves for the Fe-Cr coupling electrode in which a high Cr alloy and a low Cr alloy were placed in a single mount were also studied. The second anodic current maximum in the active region was observed on embrittled (475 degree C multiplied by 1000 hr) 26% Cr alloy and 31% Cr alloy. Pronounced first peak and second peak potentials accorded with the passivation potentials for unembrittled 50% Cr, 15% Cr alloy, respectively. Behavior of the Fe-Cr coupling electrode resembled embrittled Fe-Cr alloys.
引用
收藏
页码：22 / 28
相关论文
共 50 条
  • [1] MECHANICAL PROPERTIES OF FE-CR ALLOYS EMBRITTLED AT 475 DEGREES C
    IMAI, Y
    NISHINO, K
    NAKAGAWA, Y
    SCIENCE REPORTS OF THE RESEARCH INSTITUTES TOHOKU UNIVERSITY SERIES A-PHYSICS CHEMISTRY AND METALLURGY, 1966, S 18 : 569 - &
  • [2] PHASE DECOMPOSITION AND 475 degree C EMBRITTLEMENT IN Fe-Cr AND Fe-Cr-Co ALLOYS.
    Miyazaki, Toru
    Nakagaki, Masatoshi
    Yajima, Etsujiro
    Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals, 1974, 38 (01): : 70 - 77
  • [3] The effect of Al on the 475 °C embrittlement of Fe-Cr alloys
    Li, Wei
    Lu, Song
    Hu, Qing-Miao
    Mao, Huahai
    Johansson, Borje
    Vitos, Levente
    COMPUTATIONAL MATERIALS SCIENCE, 2013, 74 : 101 - 106
  • [4] SOLUTION CHEMISTRY IN CREVICES ON FE-CR BINARY-ALLOYS
    BOGAR, FD
    FUJII, CT
    REPORT OF NRL PROGRESS, 1974, (MAR): : 45 - 45
  • [5] Modelling of the passivation mechanism of Fe-Cr binary alloys from ac impedance and frequency resolved rrde .1. Behaviour of Fe-Cr alloys in 0.5 M H2SO4
    Annergren, I
    Keddam, M
    Takenouti, H
    Thierry, D
    ELECTROCHIMICA ACTA, 1996, 41 (7-8) : 1121 - 1135
  • [6] Modelling of the passivation mechanism of Fe-Cr binary alloys from ac impedance and frequency resolved rrde - I. Behaviour of Fe-Cr alloys in 0.5 M H2SO4
    Royal Inst of Technology, Stockholm, Sweden
    Electrochim Acta, 7-8 (1121-1135):
  • [7] ANODIC POLARIZATION BEHAVIOR OF FE-CR SURFACE ALLOYS FORMED BY ION-IMPLANTATION
    COVINO, BS
    SARTWELL, BD
    NEEDHAM, PB
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1978, 125 (03) : 366 - 369
  • [8] Modelling of the passivation mechanism of Fe-Cr binary alloys from ac impedance and frequency resolved rrde .2. Behaviour of Fe-Cr alloys in 0.5 M H2SO4 with an addition of chloride
    Annergren, I
    Keddam, M
    Takenouti, H
    Thierry, D
    ELECTROCHIMICA ACTA, 1997, 42 (10) : 1595 - 1611
  • [9] Interface microstructures of Si3N4/Fe and Fe-Cr alloys joints
    Peteves, SD
    Suganuma, K
    INTERFACE SCIENCE, 1997, 5 (01) : 63 - 72
  • [10] COMPARISON OF SOLUTION MODELS FOR NONMETALLIC SOLUTES IN BINARY LIQUID ALLOYS: NITROGEN IN Fe-Cr AND Fe-Ni.
    Lin, Jen-Chwen
    Schmid, Rainer
    Chang, Y.Austin
    Metallurgical transactions. B, Process metallurgy, 1986, 17 B (04): : 785 - 789
12345