Process for phosphate-permanganate conversion coating of Mg alloy

被引：0
|
作者：
Zhao, Ming [1 ]
Wu, Shusen [1 ]
Luo, Jirong [1 ]
Li, Dongnan [1 ]
机构：
[1] Huazhong University of Science and Technology, Wuhan 430074, China
来源：
Tezhong Zhuzao Ji Youse Hejin/Special Casting and Nonferrous Alloys | 2005年 / 25卷 / 06期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
An orthogonal design with four factors and three levels for phosphate-permanganate conversion coating of Mg alloy was performed based on the composition of Phosphate-permanganate conversion solution consisting of KMnO4, K2HPO4, H3PO4 (adjusting pH values). It was found that the H3PO4 (pH value) is dominant in micro-conversion solution, next to K2HPO4 and KMnO4, through analyzing thickness of the conversion film and thickness adhesion. And the optimized factors was obtained, so the optimization composition proportion of the phosphate-permanganate and its process were given. The experimental results showed that the corrosion resistance is equivalent to that of conversion coating in DOW1 solution.
引用
收藏
页码：328 / 329
相关论文
共 50 条
  • [1] A chromium-free conversion coating of magnesium alloy by a phosphate-permanganate solution
    Zhao, M
    Wu, SS
    Luo, JR
    Fukuda, Y
    Nakae, H
    SURFACE & COATINGS TECHNOLOGY, 2006, 200 (18-19): : 5407 - 5412
  • [2] Properties of conversion coating of magnesium alloys by a phosphate-permanganate solution
    Wu, SS
    Zhao, M
    Luo, JR
    Mao, YW
    MAGNESIUM - SCIENCE, TECHNOLOGY AND APPLICATIONS, 2005, 488-489 : 665 - 668
  • [3] A chrome-free conversion coating for magnesium-lithium alloy by a phosphate-permanganate solution
    Zhang, Hua
    Yao, Guangchun
    Wang, Shulan
    Liu, Yihan
    Luo, Hongjie
    SURFACE & COATINGS TECHNOLOGY, 2008, 202 (09): : 1825 - 1830
  • [4] Phosphate-permanganate conversion coatings on the AZ81 magnesium alloy: SEM, EIS and XPS studies
    Mosialek, M.
    Mordarski, G.
    Nowak, P.
    Simka, W.
    Nawrat, G.
    Hanke, M.
    Socha, R. P.
    Michalska, J.
    SURFACE & COATINGS TECHNOLOGY, 2011, 206 (01): : 51 - 62
  • [5] Active corrosion protection capacity of phosphate-permanganate conversion coatings doped with cerium
    Girciene, O.
    Gudaviciute, L.
    Selskis, A.
    Jasulaitiene, V.
    Martusiene, A.
    Ramanauskas, R.
    CHEMIJA, 2016, 27 (01): : 1 - 10
  • [6] Formation of phosphate/permanganate conversion coating on AZ31 magnesium alloy
    Lin, CS
    Lee, CY
    Li, WC
    Chen, YS
    Fang, GN
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2006, 153 (03) : B90 - B96
  • [7] Effect of permanganate concentration on the formation and properties of phosphate/permanganate conversion coating on AZ31 magnesium alloy
    Lee, Y. L.
    Chu, Y. R.
    Li, W. C.
    Lin, C. S.
    CORROSION SCIENCE, 2013, 70 : 74 - 81
  • [8] Conversion coating treatment for AZ31 alloy in a permanganate-phosphate solution
    Shi, Xichang
    Jarjoura, George
    Kipouros, Georges J.
    Magnesium Technology 2006, Proceedings, 2006, : 273 - 280
  • [9] Anticorrosion conversion coating content lanthanum and phosphate on foam Mg alloy
    Niu Liyuan
    Shi Zimu
    Lin Jijing
    Li Yong
    Xu Linchao
    Zhao Lan
    MATERIALS AND MANUFACTURING, PTS 1 AND 2, 2011, 299-300 : 211 - 214
  • [10] Mn oxide conversion coating on AZ31B Mg alloy with hexafluorozirconate as an inhibitor in the permanganate conversion bath
    Hsiao, Ting-Hsuan
    Lin, Chao -Sung
    APPLIED SURFACE SCIENCE, 2024, 660
12345