STUDY OF CREEP EMBRITTLEMENT OF 2-1/4Cr-1Mo STEEL WELD METAL.

被引：0
|
作者：
Swift, R.A.
Rogers, H.C.
机构：
来源：
| 1600年 / 55期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A study of creep embrittlement in 2-1/4 Cr-1 Mo steel weld metal has shown that heat treatment prior to creep has a greater effect on ductility than on rupture or creep strength. If the creep temperature is high enough to cause tempering, the rupture resistance and creep strength will be characteristic of the creep temperature. Prior heat treatment only affects weld metal strength when the temperature of creep is significantly below that of the prior heat treatment so that tempering does not occur during creep. The mechanism of creep embrittlement is shown to be related to the generation of intergranular voids. This is controlled by the formation of a denuded zone and the segregation of residual elements to the intergranular precipitate/matrix interfaces.
引用
收藏
相关论文
共 50 条
  • [1] STUDY OF CREEP EMBRITTLEMENT OF 2-1/4CR-1MO STEEL WELD METAL
    SWIFT, RA
    ROGERS, HC
    WELDING JOURNAL, 1976, 55 (07) : S188 - S198
  • [2] FATIGUE-CREEP LIFE PREDICTION OF 2-1/4CR-1MO STEEL BY INELASTIC ANALYSIS
    INOUE, T
    IGARI, T
    OKAZAKI, M
    SAKANE, M
    TOKIMASA, K
    NUCLEAR ENGINEERING AND DESIGN, 1989, 114 (03) : 311 - 321
  • [3] LOADING DIRECTION DEPENDENCE OF TEMPER EMBRITTLEMENT OBSERVED IN 2-1/4CR-1MO STEEL UNDER SUSTAINED LOADING
    SUZUKI, M
    FUKAYA, K
    OKU, T
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1983, 23 (10) : 842 - 845
  • [4] EFFECT OF HOT WORK AND CARBON CONTENT ON THE CREEP-RUPTURE STRENGTH OF WELD METAL FOR 2 1/4CR-1MO STEEL
    ASAKAWA, K
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 71 : 1377 - 1377
  • [5] PREVENTION OF TEMPER EMBRITTLEMENT IN 2 one quarter Cr-1 Mo WELD METAL.
    Grosse-Woerdemann, Josef
    Dittrich, Siegfried
    1982, (122):
  • [6] Weld repair of 2-1/4Cr-1Mo service-aged header welds
    Viswanathan, R
    Gandy, D
    Findlan, S
    JOURNAL OF PRESSURE VESSEL TECHNOLOGY-TRANSACTIONS OF THE ASME, 1999, 121 (04): : 345 - 352
  • [7] TOUGHNESS AND TEMPER EMBRITTLEMENT OF 2 one quarter Cr-1Mo WELD METAL.
    Nakanishi, Mutsuo
    Katsumoto, Norio
    Tsumura, Hiroyasu
    Yosetsu Gakkai Ronbunshu/Quarterly Journal of the Japan Welding Society, 1984, 2 (01): : 54 - 61
  • [8] EVALUATION AND SIMULATION OF THE MICROSTRUCTURAL CHANGES AND EMBRITTLEMENT IN 2-1/4CR-1MO STEEL DUE TO LONG-TERM SERVICE
    WIGNARAJAH, S
    MASUMOTO, I
    HARA, T
    ISIJ INTERNATIONAL, 1990, 30 (01) : 58 - 63
  • [9] Damage Model Determination for Predicting Creep Rupture Time of 2 1/4Cr-1Mo Steel Weld Joints
    Izuno, Hitoshi
    Demura, Masahiko
    Yamazaki, Masayoshi
    Tabuchi, Masaaki
    Abe, Daisuke
    Torigata, Keisuke
    MATERIALS TRANSACTIONS, 2021, 62 (07) : 1013 - 1022
  • [10] TEMPER EMBRITTLEMENT AND CREEP EMBRITTLEMENT OF 2 1/4 CR-1 MO SHIELDED METAL-ARC WELD DEPOSITS
    BRUSCATO, R
    WELDING JOURNAL, 1970, 49 (04) : S148 - &
12345