EFFECT OF RESIDUAL HYDROGEN CONTENT ON COLD CRACK SUSCEPTIBILITY IN WELD METAL OF HIGH STRENGTH STEELS.

被引：0
|
作者：
Matsda, Fukuhisa
Nakagawa, Hiroji
Shinozaki, Kenji
Takaba, Shinji
Kihara, Hiroshi
机构：
来源：
Transactions of JWRI (Japanese Welding Research Institute) | 1981年 / 10卷 / 02期
关键词：
WELDS - Mechanical Properties;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The residual hydrogen content was measured in the LB - TRC (Longitudinal Bead-Tensile Restraint Cracking) test specimens. The relationship between the residual hydrogen content and the lower critical stress was investigated using commerical high strength steels. The lower critical stress strongly depended on the residual hydrogen content in the weld metal.
引用
收藏
页码：55 / 63
相关论文
共 50 条
  • [1] Effect of weld metal microstructure on cold crack susceptibility of high strength weld
    Kim, Hee Jin
    Seo, Jun Seok
    Kim, Jae Hak
    Kim, Ka Hee
    Koh, Jin Hyun
    Ryoo, Hoi Soo
    Huh, Moo Young
    ADVANCED WELDING AND MICRO JOINING / PACKAGING FOR THE 21ST CENTURY, 2008, 580-582 : 13 - +
  • [2] EFFECT OF REMAINING HYDROGEN CONTENT ON COLD CRACKING SUSCEPTIBILITY IN WELD METAL OF HIGH STRENGTH STEELS - COLD CRACKING SUSCEPTIBILITY IN WELD METAL OF HY-STEEL (PART 4).
    Matsuda, Fukuhisa
    Nakagawa, Hiroji
    Shinozaki, Kenji
    Yosetsu Gakkai Ronbunshu/Quarterly Journal of the Japan Welding Society, 1987, 5 (02): : 244 - 249
  • [3] Microstructural aspect of cold crack susceptibility in high strength weld metal
    Kim, HJ
    THERMEC'2003, PTS 1-5, 2003, 426-4 : 4069 - 4074
  • [4] Effect of microstructure and chemical composition on cold crack susceptibility of high-strength weld metal
    Yi, Hui-Jun
    Lee, Yong-Jun
    Kim, Jong-Yun
    Kang, Sung-Su
    JOURNAL OF MECHANICAL SCIENCE AND TECHNOLOGY, 2011, 25 (09) : 2185 - 2193
  • [5] Effect of microstructure and chemical composition on cold crack susceptibility of high-strength weld metal
    Hui-Jun Yi
    Yong-Jun Lee
    Jong-Yun Kim
    Sung-Su Kang
    Journal of Mechanical Science and Technology, 2011, 25 : 2185 - 2193
  • [6] Effect of weld metal microstructures on cold crack susceptibility of FCAW weld metal
    Kim, Jae Hak
    Seo, Jun Seok
    Kim, Hee Jin
    Ryoo, Hoi Soo
    Kim, Ka Hee
    Huh, Moo Young
    METALS AND MATERIALS INTERNATIONAL, 2008, 14 (02) : 239 - 245
  • [7] Effect of weld metal microstructures on cold crack susceptibility of FCAW weld metal
    Jae Hak Kim
    Jun Seok Seo
    Hee Jin Kim
    Hoi Soo Ryoo
    Ka Hee Kim
    Moo Young Huh
    Metals and Materials International, 2008, 14 : 239 - 245
  • [8] CONNECTION BETWEEN COLD CRACK NUCLEI AND STRUCTURE OF WELD METAL IN HIGH-STRENGTH STEELS
    YAKUSHIN.GM
    WELDING PRODUCTION, 1973, 20 (05): : 6 - 10
  • [9] CRITERION OF ALTERNATIVE INITIATION OF COLD CRACKING IN HAZ OR WELD METAL FOR ROOT PASS WELDS OF HIGH STRENGTH STEELS.
    Matsuda, Fukuhisa
    Nakagawa, Hiroji
    Shinozaki, Kenji
    Sanematsu, Yoshihiro
    Yosetsu Gakkai Ronbunshu/Quarterly Journal of the Japan Welding Society, 1987, 5 (01): : 94 - 100
  • [10] HYDROGEN EMBRITTLEMENT OF HIGH STRENGTH STEELS.
    Mohler, J.B.
    Metal Finishing, 1981, 79 (02) : 95 - 96
12345