Determination of Fatigue Crack Lengths in Fracture Mechanics Specimens of R St 37-2 Using the Electric Potential Technique.

被引：0

|

作者：

Hagedorn, Karl Edgar

Ruediger, Ulrich

机构：

来源：

Archiv fuer das Eisenhuettenwesen | 1977年 / 48卷 / 09期

关键词：

D O I：

暂无

中图分类号：

学科分类号：

摘要：

12

引用

收藏

页码：501 / 504

相关论文

共 8 条

[1] DETERMINATION OF FATIGUE CRACK LENGTHS IN FRACTURE MECHANICS SPECIMENS OF RST37-2 USING ELECTRIC-POTENTIAL TECHNIQUE
HAGEDORN, KE
RUDIGER, U
ARCHIV FUR DAS EISENHUTTENWESEN, 1977, 48 (09): : 501 - 504
[2] Determination of the Length of Fatigue Cracks in Fracture Toughness Test Specimens Using the Electric Potential Technique.
Muellner, Rainer
Ruediger, Ulrich
Hagedorn, Karl Edgar
Archiv fuer das Eisenhuettenwesen, 1975, 46 (04): : 283 - 286
[3] DETERMINATION OF LENGTH OF FATIGUE CRACKS IN FRACTURE TOUGHNESS TEST SPECIMENS USING ELECTRIC POTENTIAL TECHNIQUE
MULLNER, R
RUDIGER, U
HAGEDORN, KE
ARCHIV FUR DAS EISENHUTTENWESEN, 1975, 46 (04): : 283 - 286
[4] EFFECT OF FATIGUE PRE-CRACKING CONDITIONS IN FRACTURE MECHANICS SPECIMENS OF STEELS ST 37-3 AND ST 52-3
DAHL, W
KRETZSCHMANN, WB
ARCHIV FUR DAS EISENHUTTENWESEN, 1976, 47 (11): : 691 - 696
[5] Determination of fracture toughness and fatigue crack growth rate using circumferentially cracked round bar specimens of Al2014T651
Neelakantha, V. L.
Jayaraju, T.
Naik, Padmayya
Kumar, Dilip K.
Rajashekar, C. R.
Mohankumar
AEROSPACE SCIENCE AND TECHNOLOGY, 2015, 47 : 92 - 97
[6] Using Direct Current Potential Drop Technique to Estimate Fatigue Crack Growth Rates in Solid Bar Specimens under Environmental Assisted Fatigue in Simulated Pressurized Water Reactor Conditions
Arrieta, Sergio
Perosanz, Francisco Javier
Barcala, Jose Miguel
Ruiz, Maria Luisa
Cicero, Sergio
METALS, 2022, 12 (12)
[7] LIFE PREDICTION OF TITANIUM AND ALUMINUM ALLOYS UNDER FRETTING FATIGUE CONDITIONS USING VARIOUS CRACK PROPAGATION CRITERIA. PART 2. APPLICATION OF THE TECHNIQUE TO CYLINDRICAL SPECIMENS WITH SEMI-ELLIPTICAL CRACK AND ACCOUNT OF THE RESIDUAL STRESSES
Khotsyanovskii, A. O.
STRENGTH OF MATERIALS, 2011, 43 (01) : 42 - 55
[8] Life prediction of titanium and aluminum alloys under fretting fatigue conditions using various crack propagation criteria. Part 2. Application of the technique to cylindrical specimens with semi-elliptical crack and account of the residual stresses
Khotsyanovskii A.O.
Strength of Materials, 2011, 43 (1) : 42 - 55