Oxidation behavior of C/C-SiC gradient matrix composites

被引：0
|
作者：
Deng, Jingyi [1 ]
Liu, Wenchuan [1 ]
Du, Haifeng [1 ]
Cheng, Huiming [1 ]
Li, Yiyi [1 ]
机构：
[1] Inst. of Metal Res., Chinese Acad. of Sci., Shenyang 110016, China
来源：
Journal of Materials Science and Technology | 2001年 / 17卷 / 05期
关键词：
Carbon matrix composites - Gradient functional materials;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The oxidation behaviors in stationary air of C/C-SiC gradient matrix composites and C/C composites were compared with each other. The results show that the oxidation threshold of C-SiC materials increases with the amount of SiC particles in the codeposition matrix. The oxidation rate of C/C-SiC gradient matrix composites is significantly lower than that of C/C material. The micro-oxidation process was observed by SEM.
引用
收藏
页码：543 / 546
相关论文
共 50 条
  • [1] Oxidation Behavior of C/C-SiC Gradient Matrix Composites
    Jingyi DENG
    Journal of Materials Science & Technology, 2001, (05) : 543 - 546
  • [2] Oxidation behavior of C/C-SiC gradient matrix composites
    Deng, JY
    Liu, WC
    Du, HF
    Cheng, HM
    Li, YY
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2001, 17 (05) : 543 - 546
  • [3] OXIDATION BEHAVIOR OF C/C-SIC COMPOSITES WITH VARIED MATRIX COMPOSITION
    Dai, J. X.
    Sha, J. J.
    Zhang, Z. F.
    Hausherr, J-M.
    Krenkel, W.
    HIGH TEMPERATURE CERAMIC MATRIX COMPOSITES 8: CERAMIC TRANSACTIONS, VOL 248, 2014, 248 : 425 - +
  • [4] Oxidation behavior of oxidation protective coatings for C/C-SiC composites at 1500°C
    Yan Zhi-qiao
    Xiong Xiang
    Xiao Peng
    Chen Feng
    Zhang Hong-bo
    Huang Bai-yun
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2009, 19 (01) : 61 - 64
  • [5] Oxidation behavior of oxidation protective coatings for C/C-SiC composites at 1500 ℃
    闫志巧
    熊翔
    肖鹏
    陈峰
    张红波
    黄伯云
    Transactions of Nonferrous Metals Society of China, 2009, 19 (01) : 61 - 64
  • [6] Ablation Behavior of (C-SiC)f/C Composites
    Zuo Ya-Zhuo
    Li Hong
    Wang Shao-Lei
    Yang Min
    Ren Mu-Su
    Sun Jin-Liang
    JOURNAL OF INORGANIC MATERIALS, 2017, 32 (11) : 1141 - 1146
  • [7] OXIDATION BEHAVIOUR OF C/C-SiC COMPOSITES IN OPEN ATMOSPHERE
    Srivastava, V. K.
    Singh, Shraddha
    ADVANCED PROCESSING AND MANUFACTURING TECHNOLOGIES FOR STRUCTURAL AND MULTIFUNCTIONAL MATERIALS II, 2009, 29 (09): : 33 - 41
  • [8] Effect of oxidation on elastic modulus of C/C-SiC composites
    Singh, S.
    Srivastava, V. K.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 486 (1-2): : 534 - 539
  • [9] Laminated C-SiC matrix composites produced by CVI
    Lackey, WJ
    King, HC
    Miller, MA
    More, KL
    INNOVATIVE PROCESSING AND SYNTHESIS OF CERAMICS, GLASSES, AND COMPOSITES, 1998, 85 : 275 - 293
  • [10] Designing with C/C-SiC composites
    Krenkel, W
    ADVANCES IN CERAMIC MATRIX COMPOSITES IX, 2003, 153 : 103 - 123
12345