Improving the Resistance of Cr18Ni10Ti Steel Components Against Corrosion Cracking.

被引：0
|
作者：
Pavlova, F.S.
Gerasimov, V.V.
Shuvalov, V.A.
机构：
来源：
Teploenergetika | 1980年 / 10期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Improvement of corrosion resistance of stainless steel components of RBMK-type boiling water reactors is attained by means of aluminum coatings. Results of corrosion tests of such coating are presented.
引用
收藏
页码：56 / 58
相关论文
共 50 条
  • [1] RAISING THE RESISTANCE TO STRESS-CORROSION CRACKING OF ELEMENTS OF CR18NI10TI STEEL
    PAVLOVA, FS
    GERASIMOV, VV
    SHUVALOV, VA
    THERMAL ENGINEERING, 1980, 27 (10) : 578 - 580
  • [2] RESISTANCE TO THERMAL FATIGUE OF CR18NI10TI STEEL
    TULYAKOV, GA
    THERMAL ENGINEERING, 1972, 19 (06) : 17 - 21
  • [3] Examples of corrosion cracking in Cr18Ni10Ti steel caused by residual stresses at bends and pittings
    Barakhtin B.K.
    Malyshev V.N.
    Inorganic Materials: Applied Research, 2016, 7 (6) : 904 - 908
  • [4] Influence of Niobium on Heat-Resistant Properties of Steel Cr18Ni10Ti
    Kvon, S. S.
    Arinova, S. K.
    Aubakirov, D. R.
    Kovaleva, T. V.
    METALLURGIST, 2023, 66 (11-12) : 1552 - 1556
  • [5] Influence of Niobium on Heat-Resistant Properties of Steel Cr18Ni10Ti
    S. S. Kvon
    S. K. Arinova
    D. R. Aubakirov
    T. V. Kovaleva
    Metallurgist, 2023, 66 : 1552 - 1556
  • [6] Embritllement of Cr18Ni10Ti Steel Irradiated with Neutrons in a Helium Atmosphere at High Temperature
    Akaev, S. O.
    Dikov, A. S.
    Kislitsin, S. B.
    Larionov, A. S.
    RUSSIAN PHYSICS JOURNAL, 2020, 62 (12) : 2365 - 2367
  • [7] Embritllement of Cr18Ni10Ti Steel Irradiated with Neutrons in a Helium Atmosphere at High Temperature
    S. O. Akaev
    A. S. Dikov
    S. B. Kislitsin
    A. S. Larionov
    Russian Physics Journal, 2020, 62 : 2365 - 2367
  • [8] Cause of corrosion cracking of steel 1Cr18Ni9Ti
    Liu, Ximing
    Lian, Jianshe
    Jinshu Rechuli/Heat Treatment of Metals, 2000, (02): : 44 - 45
  • [9] Parameters of trapping and the thermoactivated output of the deuterium ion-implanted into the Cr18Ni10Ti steel
    Karpov, SO
    Ruzhits'ky, VV
    Neklyudov, IM
    Bendikov, VI
    Tolstoluts'ka, GD
    METALLOFIZIKA I NOVEISHIE TEKHNOLOGII, 2004, 26 (12): : 1661 - 1670
  • [10] THE EFFECT OF LOCAL MICROPLASTIC DEFORMATIONS ON STRESS-CORROSION CRACKING OF 08CR18NI10TI STEEL
    MOSKVIN, LN
    EFIMOV, AA
    SHERMAN, YI
    FEDOROVA, TI
    THERMAL ENGINEERING, 1987, 34 (07) : 379 - 381
12345