Solubility of gallium sphalerite and wurtzite at 800°C and 900°C

被引：0
|
作者：
Ueno, T.
Scott, S.D.
机构：
来源：
Canadian Mineralogist | 1991年 / 29卷 / pt 1期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
相关论文
共 50 条
  • [1] SOLUBILITY OF GALLIUM IN SPHALERITE AND WURTZITE AT 800-DEGREES-C AND 900-DEGREES-C
    UENO, T
    SCOTT, SD
    CANADIAN MINERALOGIST, 1991, 29 : 143 - 148
  • [2] Oxidation behaviors of TiAlNb with coatings at 800°C and 900°C respectively
    Xiong, YM
    Zhu, SL
    Wang, FH
    RARE METAL MATERIALS AND ENGINEERING, 2006, 35 (02) : 213 - 216
  • [3] Creep deformation and mechanisms in Haynes 230 at 800 °C and 900 °C
    Pataky, Garrett J.
    Sehitoglu, Huseyin
    Maier, Hans J.
    JOURNAL OF NUCLEAR MATERIALS, 2013, 443 (1-3) : 484 - 490
  • [4] Oxidation of CrAlN thin films at 800 °C and 900 °C in air
    Kim, Min Jung
    Lee, Sang Yul
    Lee, Dong Bok
    JOURNAL OF CERAMIC PROCESSING RESEARCH, 2012, 13 : S64 - S69
  • [5] Diffusion of boron in germanium at 800-900°C
    Uppal, S
    Willoughby, AFW
    Bonar, JM
    Cowern, NEB
    Grasby, T
    Morris, RJH
    Dowsett, MG
    JOURNAL OF APPLIED PHYSICS, 2004, 96 (03) : 1376 - 1380
  • [6] Solubility of oxides in KCl melts at 800°C
    Cherginets, VL
    Rebrova, TP
    Sorochan, MA
    RUSSIAN JOURNAL OF INORGANIC CHEMISTRY, 2005, 50 (10) : 1605 - 1608
  • [7] Phase relations in the system Zn-Ga-S at 900°C and 800°C
    Ueno, T.
    Scott, S.D.
    Canadian Mineralogist, 1995, 33 (pt 1):
  • [8] Phase relations in the system Ga-Fe-S at 900°C and 800°C
    Ueno, T.
    Scott, S.D.
    Canadian Mineralogist, 1994, 32 (pt 1):
  • [9] Diffusion of boron in germanium at 800-900°C revisited
    Kipke, Felix
    Suedkamp, Tobias
    Pruessing, Jan K.
    Bougeard, Dominique
    Bracht, Hartmut
    JOURNAL OF APPLIED PHYSICS, 2020, 127 (02)
  • [10] SOLUBILITY OF HYDROGEN IN TITANIUM AT 900 DEGREES TO 1500 DEGREES C
    TAKEUCHI, S
    HONMA, T
    IKEDA, S
    SCIENCE REPORTS OF THE RESEARCH INSTITUTES TOHOKU UNIVERSITY SERIES A-PHYSICS CHEMISTRY AND METALLURGY, 1966, S 18 : 161 - &
12345