Effects of temperature, dissolved oxygen and material factor on SCC behavior of low alloy steels in high temperature water

被引：0
|
作者：
Arai, Taku [1 ]
Mayuzumi, Masami [1 ]
机构：
[1] Ctrl. Res. Inst. Elec. Pwr. Indust., 2-11-1, Iwadokita, Komae, Tokyo, 201-8511, Japan
来源：
Zairyo to Kankyo/ Corrosion Engineering | 2000年 / 49卷 / 04期
关键词：
Corrosion resistance - High temperature operations - Oxygen - Strain rate - Stress corrosion cracking - Tensile testing - Thermal effects - Water;
D O I：
10.3323/jcorr1991.49.243
中图分类号：
学科分类号：
摘要：
Stress corrosion cracking (SCC) susceptibility of heavy-thick low alloy steels was investigated by slow strain rate tensile (SSRT) tests in high temperature water containing various levels of dissolved oxygen (DO) at temperature of 373 K to 593 K. Rolled steels with high sulfur content had SCC susceptibility in the wide region of temperature-DO concentration combination, even in DO<0.005 ppm at 473 K. A forged steel with extremely low sulfur content was almost immune to SCC. SCC maps as functions of temperature and DO concentration were proposed for each steel from the SSRT tests results.
引用
收藏
页码：243 / 248
相关论文
共 50 条
  • [1] EFFECTS OF DISSOLVED OXYGEN CONCENTRATION AND TEMPERATURE ON THE STRESS CORROSION CRACKING OF LOW ALLOY STEELS IN HIGH TEMPERATURE WATER.
    Kuniya, Jiro
    Kanno, Masayoshi
    Masaoka, Isao
    Sasaki, Ryoichi
    1600, (32):
  • [2] Effects of alternating dissolved oxygen and dissolved hydrogen on the corrosion behavior of alloy 52 in high temperature high pressure water
    Nong, Jing
    Guo, Qi
    Xu, Jian
    Shoji, Tetsuo
    JOURNAL OF NUCLEAR MATERIALS, 2020, 540
  • [3] Effects of temperature and dissolved oxygen contents on fatigue lives of carbon and low alloy steels in LWR water environments
    Nakao, G
    Higuchi, M
    Kanasaki, H
    Iida, K
    Asada, Y
    EFFECTS OF THE ENVIRONMENT ON THE INITIATION OF CRACK GROWTH, 1997, 1298 : 232 - 244
  • [4] The effect of dissolved oxygen respectively dissolved hydrogen on corrosion behavior of CuCrZr alloy in high temperature water
    Huang, Yen-Jui
    Nakajima, Motoki
    Kurotaki, Hironori
    Nozawa, Takashi
    NUCLEAR MATERIALS AND ENERGY, 2022, 31
  • [5] EFFECT OF ENVIRONMENTAL AND MATERIAL CONDITIONS ON SCC OF CARBON STEELS IN HIGH TEMPERATURE WATER
    Liu, Sue
    Wright, Michael D.
    ICONE 17: PROCEEDINGS OF THE 17TH INTERNATIONAL CONFERENCE ON NUCLEAR ENGINEERING, VOL 1, 2009, : 337 - +
  • [6] Effect of temperature on corrosion fatigue behavior of low alloy pressure vessel steels in high temperature water
    Katada, Y
    Sato, S
    PROCEEDINGS OF THE EIGHTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS - WATER REACTORS, VOLS 1 AND 2, 1997, : 916 - 923
  • [7] Effect of dissolved oxygen and hydrogen on the stress corrosion cracking behavior of alloy 600 in high temperature water
    Wang, Jiamei
    Zhu, Tianyu
    Chen, Kai
    Du, Donghai
    Andresen, Peter L.
    Zhang, Lefu
    JOURNAL OF NUCLEAR MATERIALS, 2021, 543
  • [8] EFFECTS OF pH AND DISSOLVED OXYGEN ON ELECTROCHEMICAL BEHAVIOR OF STAINLESS STEEL IN HIGH TEMPERATURE WATER.
    Ohnaka, Noriyuki
    Minato, Akira
    Boshoku gijutsu, 1985, 34 (02): : 79 - 85
  • [9] Effect of dissolved oxygen on PWSCC susceptibility of Alloy 600 in high temperature water
    Wan Young Maeng
    Myoung Sik Choi
    Uh Chul Kim
    Journal of Materials Science, 2004, 39 : 655 - 657
  • [10] Effect of dissolved oxygen on PWSCC susceptibility of Alloy 600 in high temperature water
    Maeng, WY
    Choi, MS
    Kim, UC
    JOURNAL OF MATERIALS SCIENCE, 2004, 39 (02) : 655 - 657
12345