STUDY OF THE DELAMINATION BEHAVIOR OF A VERY LOW-CARBON STEEL.

被引：0
|
作者：
Bramfitt, B.L.
Marder, A.R.
机构：
来源：
Metallurgical Transactions A (Physical Metallurgy and Materials Science) | 1977年 / 8 A卷 / 08期
关键词：
IRON AND STEEL METALLOGRAPHY - ROLLING MILL PRACTICE;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Splitting, i. e. , delamination behavior, in Charpy specimens of low carbon steel was found to be caused by cracks propagating between pancake grains parallel to the rolling plane of the as-rolled plate. The results suggest that the mechanism is a decohesion of grain boundaries that is independent of the texture of the material. The number of splits increased with decreasing finishing temperature and impact-test temperature. The energy absorbed in impact testing was inversely proportional to the number of splits. In specimens annealed after rolling, splitting was evident until the material was almost completely recrystalized.
引用
收藏
页码：1263 / 1273
相关论文
共 50 条
  • [1] STUDY OF DELAMINATION BEHAVIOR OF A VERY LOW-CARBON STEEL
    BRAMFITT, BL
    MARDER, AR
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1977, 8 (08): : 1263 - 1273
  • [2] Work Softening in Low-Carbon Steel.
    Pereira Garcia do O, Alvaro Manoel
    Pirro E Longo, Waldimir
    Metalurgia, ABM (Associacao Brasileira de Metais), 1975, 31 (208): : 151 - 158
  • [3] STRAIN AGEING OF LOW-CARBON SHEET STEEL.
    Bratus', S.A.
    Uzienko, A.M.
    Fainberg, L.B.
    Smirnov, P.N.
    Metallurgist (English Translation of Metallurg), 1975, 19 (7-8): : 598 - 600
  • [4] Acoustic Properties of Low-Carbon Sheet Steel.
    Moskaleva, L.N.
    Grigorkin, O.V.
    Parfenov, A.A.
    Seleznev, V.A.
    Izvestiya Vysshikh Uchebnykh Zavedenij. Chernaya Metallurgiya, 1985, (07): : 119 - 122
  • [5] ON INTERPHASE PRECIPITATES IN A QUENCHED LOW-CARBON STEEL.
    Yankovskiy, V.M.
    Rodnikov, V.A.
    Physics of Metals and Metallography, 1979, 48 (05): : 156 - 158
  • [6] Application of the Mossbauer Effect to the Study of Retained Austenite in a Low-Carbon Steel.
    Tenuta de Azevedo, Ander Louis
    Da Silva, Eustaquio Galvao
    Metalurgia, ABM (Associacao Brasileira de Metais), 1979, 35 (255): : 91 - 96
  • [7] MICROALLOYED VERY LOW-CARBON STEEL ROD
    MCIVOR, ID
    IRONMAKING & STEELMAKING, 1989, 16 (01) : 55 - 62
  • [8] The influence of divorcing annealing on the mechanical properties of low-carbon steel.
    Howe, HM
    Levy, AG
    TRANSACTIONS OF THE AMERICAN INSTITUTE OF MINING AND METALLURGICAL ENGINEERS, 1912, 44 : 513 - 547
  • [9] ON THE HOT WORKABILITY OF LOW-CARBON Mn-Nb STEEL.
    Li, Zhengsheng
    Zheng, Zhilan
    Wang, Peixing
    Zhang, Guanyun
    Jinshu Xuebao/Acta Metallurgica Sinica, 1985, 21 (01):
  • [10] INFLUENCE OF ALLOYING ON THE AUSTENITE GRAIN GROWTH OF LOW-CARBON STEEL.
    Vinokur, B.B.
    Pilyushenko, V.L.
    Kasatkin, O.G.
    1600,
12345