Failure analysis of the fretting fatigue damage

被引：0
|
作者：
Failure Analysis Division of, CAAC-AAC, Beijing, China [1 ]
机构：
来源：
Cailiao Gongcheng | / 12卷 / 44-47期
关键词：
Cracks - Failure (mechanical) - Failure analysis - Fretting corrosion - Mechanical properties - Strength of materials;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The phenomena, effect factors and distinguishable characteristics of the failure of fretting fatigue damage have been described by real case. The failure analysis of fretting fatigue damage for soft axle of electric motor were made. The results show that the repeated damages of surface integrity and protective oxidation film is a main factor of the failure of the fretting fatigue damage.
引用
收藏
相关论文
共 50 条
  • [1] CHARACTERIZATION OF FRETTING FATIGUE DAMAGE BY SEM ANALYSIS
    GOSS, GL
    HOEPPNER, DW
    WEAR, 1973, 24 (01) : 77 - 95
  • [2] RESEARCH AND ANALYSIS ON DAMAGE OF FRETTING WEAR AND FRETTING FATIGUE FOR COMPONENTS IN NPPs
    Ning Dong
    Zhang Min
    Xie Yongchen
    He Yinbiao
    Yao Weida
    ICONE16: PROCEEDING OF THE 16TH INTERNATIONAL CONFERENCE ON NUCLEAR ENGINEERING - 2008, VOL 1, 2008, : 633 - 640
  • [3] Fretting & friction induced fatigue failure: damage criterion of polytetrafluoroethylene
    Shah, Quazi Md. Zobaer
    Chowdhury, Mohammad Asaduzzaman
    Kowser, Md. Arefin
    HELIYON, 2020, 6 (06)
  • [4] FRETTING FATIGUE FAILURE.
    Dobromirski, J.
    Smith, I.O.
    Materials Forum, 1987, 10 (04): : 256 - 263
  • [5] SCANNING ELECTRON-MICROSCOPE ANALYSIS OF FRETTING FATIGUE DAMAGE
    REEVES, RK
    HOEPPNER, DW
    WEAR, 1978, 48 (01) : 87 - 92
  • [6] On the damage mechanisms of bending fretting fatigue
    Peng, J. F.
    Zhu, M. H.
    Cai, Z. B.
    Liu, J. H.
    Zuo, K. C.
    Song, C.
    Wang, W. J.
    TRIBOLOGY INTERNATIONAL, 2014, 76 : 133 - 141
  • [7] Nondestructive characterization of fretting fatigue damage
    Neslen, CL
    Mall, S
    Sathish, S
    JOURNAL OF NONDESTRUCTIVE EVALUATION, 2004, 23 (04) : 153 - 162
  • [8] Nondestructive Characterization of Fretting Fatigue Damage
    C. L. Neslen
    S. Mall
    S. Sathish
    Journal of Nondestructive Evaluation, 2004, 23 : 153 - 162
  • [9] CHARACTERISTICS OF THE FRETTING FATIGUE DAMAGE THRESHOLD
    ADIBNAZARI, S
    HOEPPNER, DW
    WEAR, 1992, 159 (01) : 43 - 46
  • [10] DAMAGE FORMATION DURING FRETTING FATIGUE
    SATO, K
    WEAR, 1988, 125 (1-2) : 163 - 174
12345