Isothermal solidification kinetics of diffusion brazing

被引:0
|
作者
MacDonald, W.D. [1 ]
Eagar, T.W. [1 ]
机构
[1] Sherritt, Inc, Edmonton, Canada
基金
美国国家科学基金会;
关键词
Copper - Diffusion in solids - Mathematical models - Phase interfaces - Silver - Solidification;
D O I
暂无
中图分类号
学科分类号
摘要
Diffusion brazing (DB) is a process that produces interface-free joints that approach the bulk properties of the material that is to be joined. Solid-state diffusion of the melting point depressant (MPD) element into the joint metal causes the solid/liquid (S/L) interface to advance until the joint is solidified. The time required to complete this isothermal solidification stage was modeled using a moving boundary analysis. Precision measurements of the interlayer width as a function of time were made on the copper-silver system. The bonding apparatus consisted of a suspended load feedback system that prevented leakage of joint metal due to extrusion or surface wetting, thus preserving mass balance. The interlayer width vs bonding time measurements obtained were found to be within a factor of 4 of the theoretical model. The difference was ascribed to the difficulty in accurately measuring the actual liquid width and loss of silver due to vaporization. Large spherical protrusions grow during bonding, which further roughens the interface. However, experimental and predicted concentration profiles of silver were found to be in complete agreement. As the liquid remaining in the grain boundary grooves is diffused away, porosity can develop due to volume changes. By holding the joint at temperature for extended periods, complete solidification followed by homogenization will occur. Selecting the appropriate bonding temperature to achieve a specified maximum concentration of braze metal at the joint is dependent on both the isothermal solidification and homogenization kinetics.
引用
收藏
页码:315 / 325
相关论文
共 50 条
  • [1] Isothermal solidification kinetics of diffusion brazing
    MacDonald, WD
    Eagar, TW
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (01): : 315 - 325
  • [2] Isothermal solidification kinetics of diffusion brazing
    W. D. MacDonald
    T. W. Eagar
    Metallurgical and Materials Transactions A, 1998, 29 : 315 - 325
  • [3] Effect of Temperature and Sheet Temper on Isothermal Solidification Kinetics in Clad Aluminum Brazing Sheet
    Michael J. Benoit
    Mark A. Whitney
    Mary A. Wells
    Sooky Winkler
    Metallurgical and Materials Transactions A, 2016, 47 : 4425 - 4436
  • [4] Effect of Temperature and Sheet Temper on Isothermal Solidification Kinetics in Clad Aluminum Brazing Sheet
    Benoit, Michael J.
    Whitney, Mark A.
    Wells, Mary A.
    Winkler, Sooky
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2016, 47A (09): : 4425 - 4436
  • [5] KINETICS OF DIFFUSION BRAZING OF TITANIUM
    DOLGOV, YS
    SIDOKHIN, AF
    SIDOKHIN, YF
    WELDING PRODUCTION, 1968, 15 (12): : 24 - &
  • [6] DIFFUSION SOLIDIFICATION KINETICS
    SRESHTA, H
    LANGFORD, G
    APELIAN, D
    JOURNAL OF METALS, 1980, 32 (12): : 94 - 94
  • [7] Role of base-metal composition in isothermal solidification during diffusion brazing of nickel-based superalloys
    Pouranvari, M.
    Ekrami, A.
    Kokabi, A. H.
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2018, 23 (01) : 13 - 18
  • [8] Isothermal Solidification Kinetics During Transient Liquid Phase Diffusion Bonding of Single Crystal Superalloy
    Chai L.
    Hou J.
    Lang B.
    Cailiao Daobao/Materials Reports, 2020, 34 (18): : 18131 - 18134
  • [9] Comparison of diffusion kinetics during isothermal solidification and homogenisation stages of transient liquid phase bonding
    Ojo, O. A.
    Ghanbar, A.
    PHILOSOPHICAL MAGAZINE LETTERS, 2019, 99 (06) : 208 - 216
  • [10] SOLIDIFICATION BEHAVIOR DURING DIFFUSION BRAZING OF A NICKEL BASED SUPERALLOY
    Pouranvari, M.
    METAL 2009, CONFERENCE PROCEEDINGS, 2009, : 580 - 583