Accumulative roll-bonding: First experience with a twin-roll cast AA8006 alloy

被引：0
|
作者：
机构：
[1] Karlík, M.
[2] 1,Homola, P.
[3] Slámová, M.
来源：
Karlík, M. (karlik@kmat.fjfi.cvut.cz) | 1600年 / Elsevier Ltd卷 / 378期
关键词：
Crystal microstructure - Metal casting - Microhardness - Roll bonding - Scanning electron microscopy - Strength of materials - Transmission electron microscopy;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
An ultra-fine grained (UFG) material was prepared from a twin-roll cast (TRC) Al-Fe-Mn-Si (AA8006) sheet using accumulative roll-bonding (ARB) process. After initial failures to achieve good sheet bonding, five cycles of ARB at 200°C were successfully performed. Scanning electron microscopy (Electron Backscatter Diffraction) and transmission electron microscopy (TEM) were used for the characterization of subgrain and grain structures of ARB processed samples. The strength of ARB sheets was evaluated by microhardness measurements. Very fine grain structure (0.4-0.8μm) with large disorientation was observed after two cycles of ARB. In two samples, areas with extremely fine grains 0.1-0.3μm in diameter were found. The hardness of the alloy increased from 28 to 60 HV1 after the first two cycles, but during subsequent ARB processing it rose only very slightly. © 2004 Elsevier B.V. All rights reserved.
引用
收藏
页码：1 / 2
相关论文
共 50 条
  • [1] Accumulative roll-bonding:: first experience with a twin-roll cast AA8006 alloy
    Karlík, M
    Homola, P
    Slámová, M
    JOURNAL OF ALLOYS AND COMPOUNDS, 2004, 378 (1-2) : 322 - 325
  • [2] Annealing Effects in Twin-Roll Cast AA8006 Aluminium Sheets Processed by Accumulative Roll-Bonding
    Cieslar, Miroslav
    Pokova, Michaela
    MATERIALS, 2014, 7 (12) : 8058 - 8069
  • [3] Effect of the temperature of accumulative roll bonding on the microstructure and properties of twin-roll cast AA8006 alloy
    Homola, P
    Slámová, M
    Karlík, M
    Cizek, J
    Procházka, I
    NANOMATERIALS BY SEVERE PLASTIC DEFORMATION, 2006, 503-504 : 281 - 286
  • [4] Influence of homogenization on the microstructure, mechanical properties and texture of the twin-roll cast AA8006 sheet processed by accumulative roll-bonding
    Karlik, Miroslav
    Homola, Petr
    Slama, Peter
    Capek, Jiri
    Harcuba, Petr
    17TH INTERNATIONAL CONFERENCE ON ALUMINIUM ALLOYS 2020 (ICAA17), 2020, 326
  • [5] Impact of as-cast structure on structure and properties of twin-roll cast AA8006 alloy
    Slamova, M.
    Juricek, Z.
    Ocenasek, V.
    Materials Science Forum, 2000, 331 (I) : 161 - 166
  • [6] Impact of as-cast structure on structure and properties of twin-roll cast AA8006 alloy
    Slámová, M.
    Juříček, Z.
    Očenášek, V.
    Materials Science Forum, 2000, 331
  • [7] Impact of as-cast structure on structure and properties of twin-roll cast AA8006 alloy
    Slámová, M
    Juricek, Z
    Ocenásek, V
    ALUMINIUM ALLOYS: THEIR PHYSICAL AND MECHANICAL PROPERTIES, PTS 1-3, 2000, 331-3 : 161 - 166
  • [8] Homogenization of twin-roll cast A8006 alloy
    Chen Zhong-wei
    Li Shi-shun
    Zhao Jing
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2012, 22 (06) : 1280 - 1285
  • [9] Accumulative roll bonding of AA8006, AA8011 and AA5754 sheets
    Slamova, M.
    Homola, P.
    Slama, P.
    Karlik, M.
    Cieslar, M.
    Ohara, Y.
    Tsuji, N.
    ALUMINIUM ALLOYS 2006, PTS 1 AND 2: RESEARCH THROUGH INNOVATION AND TECHNOLOGY, 2006, 519-521 : 1227 - 1232
  • [10] Differences in structure evolution of twin-roll cast AA8006 and AA8011 alloys during annealing
    Slámová, M
    Ocenásek, V
    Cieslar, M
    Chalupa, B
    Merle, P
    ALUMINIUM ALLOYS: THEIR PHYSICAL AND MECHANICAL PROPERTIES, PTS 1-3, 2000, 331-3 : 829 - 834
12345